Avoiding low austenite fractions and nitride formation are major challenges in laser welding of duplex stainless steels (DSS). The present research aims at investigating efficient means of promoting austenite formation during autogenous laser welding of DSS without sacrificing productivity. In this study, effects of shielding gas and laser reheating were investigated in welding of 1.5-mm-thick FDX 27 (UNS S82031) DSS. Four conditions were investigated: Ar-shielded welding, N2-shielded welding, Ar-shielded welding followed by Ar-shielded laser reheating, and N2-shielded welding followed by N2-shielded laser reheating. Optical microscopy, thermodynamic calculations, and Gleeble heat treatment were performed to study the evolution of microstructure and chemical composition. The austenite fraction was 22% for Ar-shielded and 39% for N2-shielded as-welded conditions. Interestingly, laser reheating did not significantly affect the austenite fraction for Ar shielding, while the austenite fraction increased to 57% for N2-shielding. The amount of nitrides was lower in N2-shielded samples compared to in Ar-shielded samples. The same trends were also observed in the heat-affected zone. The nitrogen content of weld metals, evaluated from calculated equilibrium phase diagrams and austenite fractions after Gleeble equilibrating heat treatments at 1100 °C, was 0.16% for N2-shielded and 0.11% for Ar-shielded welds, confirming the importance of nitrogen for promoting the austenite formation during welding and especially reheating. Finally, it is recommended that combining welding with pure nitrogen as shielding gas and a laser reheating pass can significantly improve austenite formation and reduce nitride formation in DSS laser welds.

The present research was aimed at simultaneous increase in strength and fracture energy of friction stir spot weld of Al-5083 alloy via reinforcing by Fe 3 O 4 nanoparticles. Compared to nonreinforced welds, failure load and fracture energy of reinforced welds increased up to ∼ 115 and 560%, respectively. These findings were discussed in the light of grain refinement as well as considerable increase in hardness of fracture location due to the presence of sub-micron and nano reinforcing particles (RPs). Fe 3 O 4 nanoparticles were transformed to Al-Fe intermetallics due to their small size and heat generated during the welding process. The stir zone of reinforced welds consisted of three different grain structures among which the finest one was related to the composite structure containing well-distributed RPs in the aluminium matrix.

No abstract

Duplex stainless steel (DSS) blocks with dimensions of 150 × 70x30 mm3 were fabricated by Laser Metal Deposition with Wire (LMDw). Implementation of a programmable logic control system and the hot-wire technology provided a stable and consistent process producing high-quality and virtually defect-free deposits. Microstructure and mechanical properties were studied for as-deposited (AD) material and when heat-treated (HT) for 1 h at 1100 °C. The AD microstructure was inhomogeneous with highly ferritic areas with nitrides and austenitic regions with fine secondary austenite occurring in a periodic manner. Heat treatment produced a homogenized microstructure, free from nitrides and fine secondary austenite, with balanced ferrite and austenite fractions. Although some nitrogen was lost during LMDw, heat treatment or reheating by subsequent passes in AD allowed the formation of about 50% austenite. Mechanical properties fulfilled common requirements on strength and toughness in both as-deposited and heat-treated conditions achieving the highest strength in AD condition and best toughness and ductility in HT condition. Epitaxial ferrite growth, giving elongated grains along the build direction, resulted in somewhat higher toughness in both AD and HT conditions when cracks propagated perpendicular to the build direction. It was concluded that high-quality components can be produced by LMDw and that deposits can be used in either AD or HT conditions. The findings of this research provide valuable input for the fabrication of high-performance DSS AM components. Graphical Abstract

A systematic four-stage methodology was developed and applied to the Laser Metal Deposition with Wire (LMDw) of a duplex stainless steel (DSS) cylinder > 20 kg. In the four stages, single-bead passes, a single-bead wall, a block, and finally a cylinder were produced. This stepwise approach allowed the development of LMDw process parameters and control systems while the volume of deposited material and the geometrical complexity of components increased. The as-deposited microstructure was inhomogeneous and repetitive, consisting of highly ferritic regions with nitrides and regions with high fractions of austenite. However, there were no cracks or lack of fusion defects; there were only some small pores, and strength and toughness were comparable to those of the corresponding steel grade. A heat treatment for 1 h at 1100 °C was performed to homogenize the microstructure, remove nitrides, and balance the ferrite and austenite fractions compensating for nitrogen loss occurring during LMDw. The heat treatment increased toughness and ductility and decreased strength, but these still matched steel properties. It was concluded that implementing a systematic methodology with a stepwise increase in the deposited volume and geometrical complexity is a cost-effective way of developing additive manufacturing procedures for the production of significantly sized metallic components.