The interest in thermoplastic starch (TPS) as a substitute material to replace conventional thermoplastics continues especially due its biodegradability, availability, low cost and because it is obtained from renewable sources. However, its poor mechanical properties and its high sensitivity to humidity have limited its use in several applications. Here, the copolymer poly (ethylene-covinyl alcohol) (EVOH), with two different ethylene contents, 27 and 44 mol% were blended with TPS by extrusion in order to overcome these limitations. The obtained blends were characterized by thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), mechanical tensile testing, Scanning Electron Microscopy (SEM) and moisture absorption test. The addition of EVOH copolymer did not significantly changed the thermal stability of TPS, however it increased the tensile strength in 65% when compared to TPS. The morphology of the blends did not showed two distinct phases, an indication of miscibility or partial miscibility of the components. A decrease of moisture absorption was obtained by the addition of EVOH and is more pronounced for the EVOH with 44% of ethylene.

O crescente uso do amido como um material termoplástico tem despertado o interesse por esse polímero especialmente devido sua biodegradabilidade e por ser obtido de fontes renováveis. Porém suas propriedades mecânicas inferiores e a alta sensibilidade a umidade têm limitado sua utilização em diversas aplicações. O desenvolvimento de blendas poliméricas tem sido uma boa alternativa para obtenção de novos materiais à base de amido com suas propriedades melhoradas. Blendas de amido termoplástico (TPS) e poli(álcool vinílico -co-etileno) (EVOH), com 27 e 44%mol de etileno, foram obtidas em uma extrusora de rosca simples. O TPS foi produzido pela mistura de amido de milho e glicerol como plastificante (70:30). Para a obtenção das blendas foram acrescentados 5, 10 e 15% (m/m) do EVOH27% e EVOH44%, obtendo assim 6 blendas de diferentes composições. As técnicas de análise térmica dinâmico mecânica (DMTA), espectroscopia de infravermelho por transformada de Fourier (FTIR) e de microscopia eletrônica de varredura (MEV) foram empregadas para a verificação de possível miscibilidade da mistura. A existência de uma única Tg nas blendas foi um indicativo de um sistema miscível, porém os espectros de infravermelho não apresentaram deslocamento de bandas sendo muito semelhantes ao espectro soma que indica um material totalmente imiscível, nas imagens obtidas pelo MEV não ficou evidente a presença de duas ou mais fases, porém podem ter sido disfarçadas devido à similaridade da morfologia de ambos materiais. As análises termogravimétricas (TGA) não mostraram alterações na estabilidade térmica das blendas. A técnica de difração de raios-X mostrou que não houve um aumento significativo na cristalinidade das blendas em relação ao TPS. As blendas condicionadas em ambientes com umidades relativas controladas apresentaram redução na absorção de umidade e no coeficiente de difusão de água com o aumento do teor de EVOH e de etileno na sua composição. Com o aumento do teor de EVOH, foi observado um aumento na resistência mecânica à tração das blendas e uma redução no alongamento na ruptura e no módulo de elasticidade quando comparados com o TPS puro. The increasing use of starch as a thermoplastic material has aroused interest in this polymer especially due to its biodegradability and because it is obtained from renewable sources. However, its lower mechanical properties and the high sensitivity to humidity have limited its use in several applications. The development of polymer blends has been a good alternative to obtain new starch-based materials with their properties improved. Blends of thermoplastic starch (TPS) and poly (vinyl alcoholethylene) (EVOH) with 27 and 44 mol% of ethylene were obtained in a single-screw extruder. TPS was produced by mixing corn starch and glycerol as plasticizer (70:30). To obtain the blends, 5, 10 and 15% (w/w) of EVOH27% and EVOH44% were added, thus obtaining 6 blends with different compositions. Mechanical dynamic thermal analysis (DMTA), Fourier transform infrared spectroscopy (FTIR) and scanning electr...

Las cañas de bambú son un material de construcción único para diversos tipos de estructuras y cada vez hay una mayor aceptación de los bambúes para usos estructurales. Sin embargo, tienen como inconveniente su propensión al ataque por insectos. En este trabajo se hizo un estudio de la eficacia de tres diferentes tipos de preservadores: 1) químicos tradicionales, 2) naturales de bajo riesgo para el ser humano y 3) térmicos a diferentes temperaturas, para prevenir el ataque del insecto escarabajo Dinoderus minutus al bambú de la especie Bambusa vulgaris vittata. Los dos primeros tratamientos se realizaron por inmersión y el tipo térmico fue hecho por el proceso de secado. Cada dos semanas, se evaluó el ataque a tres especímenes de cada tratamiento, incluyendo los correspondientes a un testigo sin elemento preservador alguno. Los resultados mostraron que la mayoría de los tratamientos por inmersión fueron eficaces, reduciendo considerablemente el ataque de los insectos en comparación con el testigo.En cuanto al tratamiento térmico, las temperaturas menores o iguales a 130 °C no mostraron ser eficaces; las temperaturas de 190 °C y 210 °C revelaron eficacias aceptables.