Ba0.92Ca0.08Ti0.95Zr0.05O3 (BCZT8-5) ceramic materials have been scarcely studied as lead-free piezo/ferroelectrics despite their enhanced Curie temperature (>100 °C) with respect to most studied BCZT compositions. In this work, homogeneous dense BCZT8-5 ceramics with grain size in the range of 20 μm, and optimum ferroelectric, dielectric, and electromechanical performance, were prepared by the mixed oxides route using moderate synthesis (1250 °C-2 h) and sintering (1400 °C-2 h) conditions. Thickness-poled thin disks and monomodal shear plate resonators were used for the determination of piezoelectric coefficients, coupling factors, elastic, and dielectric permittivity coefficients, including all losses, by iterative analysis of impedance curves at resonance. Furthermore, the thermal evolution of the piezoelectric characteristics at resonance was determined to assess the enhanced working range of the ceramics (≈100 °C). Ferroelectric hysteresis loops and strains vs. electric-field butterfly loops were also measured and showed soft behavior with Ec = 2 kV/cm, Pr = 12 μC/cm2 after a maximum applied field of 3 kV was used. The ceramics showed a high endurance of P-E cycles to electrical fatigue up to 107 cycles. Moreover, dielectric properties as a function of temperature were also accomplished and showed nearly normal ferroelectric behavior, characteristic of samples with low crystallographic disorder. Overall, these ceramics showed high sensitivity and higher stability than other currently studied BCZT compositions.