The present study demonstrates the possibility of fabricating zirconia parts with a complex shape and internal architecture using a low-cost stereolithography-based technique. One of the critical steps in ceramics stereolithography is the preparation of a photo-curable slurry with properties that fulfill specific requirements, such as having a low viscosity, high solids loading and appropriate curing characteristics. Slurries with different acrylic monomers and ceramic fillers were studied concerning their rheological and curing behavior. New formulations based on mono- and tri-functional acrylic monomers revealed the following excellent rheological properties: The viscosity of the mono-/tri-acrylate-based slurry with 75 wt.% of zirconia was 1.6 Pa·s at 30 s−1. Zirconia stabilized with 3 mol.% yttria was found to be more favorable than zirconia with 8 mol.% yttria for slurry preparation, because of its lower surface area and higher tapped density. It was shown that the cure depth of the suspensions was suitable for printing objects with a 50 µm layer thickness, good interlayers connection and surface finishing.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.