Opto-electronics on/with paper is fostering a novel generation of flexible and recyclable devices for sunlight harvesting and intelligent optical sensing.

Metallic nanoparticles (NPs) have received recently considerable interest of photonic and photovoltaic communities. In this work, we report the optoelectronic properties of gold NPs (Au-NPs) obtained by depositing very thin gold layers on glass substrates through thermal evaporation electron-beam assisted process. The effect of mass thickness of the layer was evaluated. The polycrystalline Au-NPs, with grain sizes of 14 and 19 nm tend to be elongated in one direction as the mass thickness increase. A 2 nm layer deposited at 250°C led to the formation of Au-NPs with 10-20 nm average size, obtained by SEM images, while for a 5 nm layer the wide size elongates from 25 to 150 nm with a mean at 75 nm. In the near infrared region was observed an absorption enhancement of amorphous silicon films deposited onto the Au-NPs layers with a corresponding increase in the PL peak for the same wavelength region.

For analytical applications in portable sensors to be used in the point-of-need, low-cost SERS substrates using paper as a base, are an alternative. In this work, SERS substrates were produced on two different types of paper: a high porosity paper (Whatman no. 1); and a low porosity paper (commercially available office paper, Portucel Soporcel). Solutions containing spherical silver nanoparticles (AgNPs) and silver nanostars (AgNSs) were separately drop-casted on hydrophilic wells patterned on the papers. The porosity of the paper was found to play a determinant role on the AgNP and AgNS distribution along the paper fibres, with most of the nanoparticles being retained at the illuminated surface of the office paper substrate. The highest SERS enhancements were obtained for the office paper substrate, with deposited AgNSs. A limit of detection for rhodamine-6G as low as 11.4 ± 0.2 pg could be achieved, with an analytical enhancement factor of ≈107 for this specific analyte. The well patterning technique allowed good signal uniformity (RSD of 1.7%). Besides, these SERS substrates remained stable after 5 weeks of storage (RSD of 7.3%). Paper-induced aggregation of AgNPs was found to be a viable alternative to the classical salt-induced aggregation, to obtain a highly sensitive SERS substrates.

In the present work, tracing and Whatman papers were used as substrates to grow zinc oxide (ZnO) nanostructures. Cellulose-based substrates are cost-efficient, highly sensitive and environmentally friendly. ZnO nanostructures with hexagonal structure were synthesized by hydrothermal under microwave irradiation using an ultrafast approach, that is, a fixed synthesis time of 10 min. The effect of synthesis temperature on ZnO nanostructures was investigated from 70 to 130 °C. An Ultra Violet (UV)/Ozone treatment directly to the ZnO seed layer prior to microwave assisted synthesis revealed expressive differences regarding formation of the ZnO nanostructures. Structural characterization of the microwave synthesized materials was carried out by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The optical characterization has also been performed. The time resolved photocurrent of the devices in response to the UV turn on/off was investigated and it has been observed that the ZnO nanorod arrays grown on Whatman paper substrate present a responsivity 3 times superior than the ones grown on tracing paper. By using ZnO nanorods, the surface area-to-volume ratio will increase and will improve the sensor sensibility, making these types of materials good candidates for low cost and disposable UV sensors. The sensors were exposed to bending tests, proving their high stability, flexibility and adaptability to different surfaces.

No abstract