Catalysts based on single atoms of scarce precious metals can lead to more efficient use through enhanced reactivity and selectivity. However, single atoms on catalyst supports can be mobile and aggregate into nanoparticles when heated at elevated temperatures. High temperatures are detrimental to catalyst performance unless these mobile atoms can be trapped. We used ceria powders having similar surface areas but different exposed surface facets. When mixed with a platinum/aluminum oxide catalyst and aged in air at 800°C, the platinum transferred to the ceria and was trapped. Polyhedral ceria and nanorods were more effective than ceria cubes at anchoring the platinum. Performing synthesis at high temperatures ensures that only the most stable binding sites are occupied, yielding a sinter-resistant, atomically dispersed catalyst.

To improve fuel efficiency, advanced combustion engines are being designed to minimize the amount of heat wasted in the exhaust. Hence, future generations of catalysts must perform at temperatures that are 100°C lower than current exhaust-treatment catalysts. Achieving low-temperature activity, while surviving the harsh conditions encountered at high engine loads, remains a formidable challenge. In this study, we demonstrate how atomically dispersed ionic platinum (Pt) on ceria (CeO), which is already thermally stable, can be activated via steam treatment (at 750°C) to simultaneously achieve the goals of low-temperature carbon monoxide (CO) oxidation activity while providing outstanding hydrothermal stability. A new type of active site is created on CeO in the vicinity of Pt, which provides the improved reactivity. These active sites are stable up to 800°C in oxidizing environments.

Metal nanoparticles contain the active sites in heterogeneous catalysts, which are important for many industrial applications including the production of clean fuels, chemicals and pharmaceuticals, and the cleanup of exhaust from automobiles and stationary power plants. Sintering, or thermal deactivation, is an important mechanism for the loss of catalyst activity. This is especially true for high temperature catalytic processes, such as steam reforming, automotive exhaust treatment, or catalytic combustion. With dwindling supplies of precious metals and increasing demand, fundamental understanding of catalyst sintering is very important for achieving clean energy and a clean environment, and for efficient chemical conversion processes with atom selectivity. Scientists have proposed two mechanisms for sintering of nanoparticles: particle migration and coalescence (PMC) and Ostwald ripening (OR). PMC involves the mobility of particles in a Brownian-like motion on the support surface, with subsequent coalescence leading to nanoparticle growth. In contrast, OR involves the migration of adatoms or mobile molecular species, driven by differences in free energy and local adatom concentrations on the support surface. In this Account, we divide the process of sintering into three phases. Phase I involves rapid loss in catalyst activity (or surface area), phase II is where sintering slows down, and phase III is where the catalyst may reach a stable performance. Much of the previous work is based on inferences from catalysts that were observed before and after long term treatments. While the general phenomena can be captured correctly, the mechanisms cannot be determined. Advancements in the techniques of in situ TEM allow us to observe catalysts at elevated temperatures under working conditions. We review recent evidence obtained via in situ methods to determine the relative importance of PMC and OR in each of these phases of catalyst sintering. The evidence suggests that, in phase I, OR is responsible for the rapid loss of activity that occurs when particles are very small. Surprisingly, very little PMC is observed in this phase. Instead, the rapid loss of activity is caused by the disappearance of the smallest particles. These findings are in good agreement with representative atomistic simulations of sintering. In phase II, sintering slows down since the smallest particles have disappeared. We now see a combination of PMC and OR, but do not fully understand the relative contribution of each of these processes to the overall rates of sintering. In phase III, the particles have grown large and other parasitic phenomena, such as support restructuring, can become important, especially at high temperatures. Examining the evolution of particle size and surface area with time, we do not see a stable or equilibrium state, especially for catalysts operating at elevated temperatures. In conclusion, the recent literature, especially on in situ studies, shows that OR is the dominant process causing the growth of nanoparticle size....

Catalysis by single isolated atoms of precious metals has attracted much recent interest, as it promises the ultimate in atom efficiency. Most previous reports are on reducible oxide supports. Here we show that isolated palladium atoms can be catalytically active on industrially relevant g-alumina supports. The addition of lanthanum oxide to the alumina, long known for its ability to improve alumina stability, is found to also help in the stabilization of isolated palladium atoms. Aberration-corrected scanning transmission electron microscopy and operando X-ray absorption spectroscopy confirm the presence of intermingled palladium and lanthanum on the g-alumina surface. Carbon monoxide oxidation reactivity measurements show onset of catalytic activity at 40°C. The catalyst activity can be regenerated by oxidation at 700°C in air. The high-temperature stability and regenerability of these ionic palladium species make this catalyst system of potential interest for low-temperature exhaust treatment catalysts.

Single-atom catalysts have attracted attention because of improved atom efficiency, higher reactivity, and better selectivity. A major challenge is to achieve high surface concentrations while preventing these atoms from agglomeration at elevated temperatures. Here we investigate the formation of Pt single atoms on an industrial catalyst support. Using a combination of surface sensitive techniques such as XPS and LEIS, X-ray absorption spectroscopy, electron microscopy, as well as density functional theory, we demonstrate that cerium oxide can support Pt single atoms at high metal loading (3 wt % Pt), without forming any clusters or 3D aggregates when heated in air at 800 °C. The mechanism of trapping involves a reaction of the mobile PtO2 with under-coordinated cerium cations present at CeO2(111) step edges, allowing Pt to achieve a stable square planar configuration. The strong interaction of mobile single-atom species with the support, present during catalyst sintering and regeneration, helps explain the sinter resistance of ceria-supported metal catalysts.