Sugarcane bagasse ash (SCBA) is an industrial waste that contains silicon and aluminum oxides as the major components and iron, calcium, magnesium, and potassium oxides as the main minor components. In this paper, SCBA from one Brazilian factory was characterized and tested for its influence on the ceramic properties of clay/ash ceramic probes. Prismatic probes were pressed (18 MPa) using a ceramic mass mixed with 0%, 5%, 8%, and 10% ash. The probes were fired at temperatures between 800° and 1200°C. X‐ray diffraction, X‐ray fluorescence, thermal analysis (differential thermal analysis, thermogravimetric analysis/differential thermogravimetric analysis), and tests for texture (particle‐size analysis), flexural strength, and linear shrinkage were carried out to characterize the samples. The results showed that the amount of ash to be incorporated will depend on mainly the composition of clay but also ash, and indicated that the clay used in this work can incorporate up to 10% weight of ash to produce solid bricks. The results also showed an improvement in ceramic/ash properties up to sintering temperatures higher than 1000°C.
The fabrication of boring tools ͑burrs͒ for dentistry with the use of a hot-filament chemical vapor deposition ͑CVD͒ system, to form the diamond abrading structure, is reported here. The diamond was synthesized from a methane/freon gas mixture diluted in hydrogen. Comparative drilling tests with conventional diamond burrs and the CVD diamond burrs in borosilicate glasses demonstrated a lifetime more than 20 times larger for the CVD diamond burrs. Also, heat flow experiments in dentine showed that the CVD diamond burrs induce temperature gradients of the same order as the conventional ones. These characteristics of the CVD diamond burrs are highly desirable for odontological applications where the burrs' lifetime and the low temperature processing are essential to the quality and comfort of the treatment.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.