Major new insights on electrochemical processes at graphite electrodes are reported, following extensive investigations of two of the most studied redox couples, Fe(CN) 6 4−/3− and Ru(NH 3 ) 6 3+/2+ . Experiments have been carried out on five different grades of highly oriented pyrolytic graphite (HOPG) that vary in step-edge height and surface coverage. Significantly, the same electrochemical characteristic is observed on all surfaces, independent of surface quality: initial cyclic voltammetry (CV) is close to reversible on freshly cleaved surfaces (>400 measurements for Fe(CN) 6 4−/3− and >100 for Ru(NH 3 ) 6 3+/2+ ), in marked contrast to previous studies that have found very slow electron transfer (ET) kinetics, with an interpretation that ET only occurs at step edges. Significantly, high spatial resolution electrochemical imaging with scanning electrochemical cell microscopy, on the highest quality mechanically cleaved HOPG, demonstrates definitively that the pristine basal surface supports fast ET, and that ET is not confined to step edges. However, the history of the HOPG surface strongly influences the electrochemical behavior. Thus, Fe(CN) 6 4−/3− shows markedly diminished ET kinetics with either extended exposure of the HOPG surface to the ambient environment or repeated CV measurements. In situ atomic force microscopy (AFM) reveals that the deterioration in apparent ET kinetics is coupled with the deposition of material on the HOPG electrode, while conducting-AFM highlights that, after cleaving, the local surface conductivity of HOPG deteriorates significantly with time. These observations and new insights are not only important for graphite, but have significant implications for electrochemistry at related carbon materials such as graphene and carbon nanotubes.

The expansion of lithium-ion batteries from consumer electronics to larger-scale transport and energy storage applications has made understanding the many mechanisms responsible for battery degradation increasingly important. The literature in...

After all, it's active: High‐resolution scanning electrochemical cell microscopy (SECCM) demonstrates that electron transfer at the basal plane of highly oriented pyrolytic graphite (HOPG) is fast. This finding requires radical revision of the current textbook model for HOPG electrochemistry.

The electro-oxidation of dopamine (DA) is investigated on the unmodified surfaces of five different classes of carbon electrodes: glassy carbon (GC), oxygen-terminated polycrystalline boron-doped diamond (pBDD), edge plane pyrolytic graphite (EPPG), basal plane pyrolytic graphite (BPPG), and the basal surface of highly oriented pyrolytic graphite (HOPG), encompassing five distinct grades with step edge density and coverage varying by more than 2 orders of magnitude. Surfaces were prepared carefully and characterized by a range of techniques, including atomic force microscopy (AFM), field emission scanning electron microscopy (FE-SEM), and Raman spectroscopy. Although pBDD was found to be the least susceptible to surface fouling (even at relatively high DA concentrations), the reaction showed sluggish kinetics on this electrode. In contrast, DA electro-oxidation at pristine basal plane HOPG at concentrations ≤100 μM in 0.15 M PBS, pH 7.2, showed fast kinetics and only minor susceptibility toward surface fouling from DA byproducts, although the extent of HOPG surface contamination by oxidation products increased substantially at higher concentrations (with the response similar on all grades, irrespective of step edge coverage). EPPG also showed a fast response, with little indication of passivation with repeated voltammetric cycling but a relatively high background signal due to the high capacitance of this graphite surface termination. Of all five carbon electrode types, freshly cleaved basal plane HOPG showed the clearest signal (distinct from the background) at low concentrations of DA (<10 μM) as a consequence of the low capacitance. Studies of the electrochemical oxidation of DA in the presence of the common interferents ascorbic acid (AA) and serotonin (5-HT), of relevance to neurochemical analysis, showed that the signals for DA were still clearly and easily resolved at basal plane HOPG surfaces. In the presence of AA, repetitive voltammetry caused products of AA electro-oxidation to adsorb onto the HOPG surface, forming a permselective film that allowed the electrochemical oxidation of DA to proceed unimpeded, while greatly inhibiting the electrochemical response of AA itself. The studies presented provide conclusive evidence that the pristine surface of basal plane HOPG is highly active for the detection of DA, irrespective of the step edge density and method of cleavage, and adds to a growing body of evidence that the basal plane of HOPG is a much more active electrode for many classes of electrode reactions than previously believed.