Mikrostruktura i odporność na zużycie powłok natryskiwanych metodą płomieniowo-proszkową mieszaninami proszkówMicrostructure and wear resistance of flame sprayed with the powder mixture coatings

Functional performance of thermally sprayed coatings depends to a large degree on their surface topography. Surface topography of coatings was studied by analyzing numerically data sets aquired by contact profilometry. The effect of spraying method and powder composition was explored for a range of coatings. The effect of coating composition was studied for cermet coatings flame sprayed with mixtures of Ni‐5%Al with ZrO2‐30%CaO. To characterize the coating surface topography, multifractal analysis was performed. (© 2009 Wiley‐VCH Verlag GmbH & Co. KGaA, Weinheim)

Mikrostruktura powłok cermetalowych natryskiwanych metodą płomieniowo-proszkowąMicrostructure of flame sprayed cermet coatings Dr hab. tadeusz Hejwowski, prof. PL, mgr inż. anna Łabacz-Kęcik -Politechnika Lubelska. StreszczenieW artykule przedstawiono wyniki badań mikrostruktury powłok natryskiwanych metodą płomieniowo-proszkową mieszaninami proszków nimoAl/ZrO 2 -30% CaO oraz niAlmo/Al 2 O 3 -40% TiO 2 . Skład fazowy określono metodą XRD i wykazano, że w powłoce ZrO 2 -30% CaO występują fazy ZrO 2 oraz CaZrO 3 , a w powłoce Al 2 O 3 -40% TiO 2 -β tytanian glinu, korund, rutyl. Porowatość powłok cermetalowych zależała od składu proszków zastosowanych do natryskiwania. Wartości parametrów struktury geometrycznej powierzchni malały ze wzrastającą zawartością materiału ceramicznego. Dodanie do materiału bazowego tworzącego osnowę cermetalu niewielkiej ilości innego materiału zmienia mechanizm formowania powłoki.