Porous aluminum foams were successfully fabricated following the space-holder powder metallurgy method with a solar sintering stage. Al foams with porosities of 50, 60, and 70 vol.% were sintered in a low-cost Fresnel lens. Green parts were prepared using aluminum powder as the main metallic material and saccharose as a soluble space-holder. The dissolution stage was designed for each foam and required longer periods of time, between 8 and 32 h, as the design porosity increased. Brown parts were fully sintered by concentrated solar energy at a lower temperature (500 °C) and for shorter times (12–20 min) than those required by conventional sintering techniques (640 °C, ~9 h). The evaluation of density and the characterization of pore size and distribution in the sintered foams was carried out. All obtained foams were stable and presented a homogeneously distributed porosity, very close to the design porosity, with differences lower than 2.1 vol.%, and with approximately half being characterized as open porosity. Moreover, the solar sintered foams presented a high quality, and similar or even greater mechanical properties (such as compressive strength and impact energy absorption) than those achieved by conventional techniques. Foams with 50 vol.% of porosity exhibited the best mechanical behavior, in terms of impact-energy absorption (24.42 MJ/m3) and compressive strength (27.4 MPa).

Material Extrusion Additive Manufacturing (MEAM) is a novel technology to produce polymeric, metallic, and ceramic complex components. Filaments composed of a high-volume content of metal powder and a suitable binder system are needed to obtain metallic parts. Thermal and energetic controversies do not affect MEAM technology, although common in other additive manufacturing (AM) techniques. High thermal conductivity and reflectivity of copper to high-energy beams are the most challenging properties. A material extrusion technique to produce high density and quality copper parts is deeply studied in this research. Characterization of the filament, printed parts, brown parts and final sintered parts is provided. The sintering stage is evaluated through density analysis of the sintered copper parts, as well as their dimensional accuracy after part shrinkage inherent to the sintering process. The mechanical behavior of sintered parts is assessed through tensile, hardness and impact toughness tests. In addition, the measured electrical and thermal conductivities are compared to those obtained by other AM technologies. High-density components, with 95% of relative density, were successfully manufactured using MEAM technology. Similar or even superior mechanical, thermal and electrical properties than those achieved by other 3D printing processes such as Electron Beam Melting, Selective Laser Melting and Binder Jetting were obtained.