Ionic liquids (ILs) have shown to be promising additives to the catalyst layer to enhance oxygen reduction reaction in polymer electrolyte fuel cells. However, fundamental understanding of their role in complex catalyst layers in practically relevant membrane electrode assembly environment is needed for rational design of highly durable and active platinum-based catalysts. Here we explore three imidazolium-derived ionic liquids, selected for their high proton conductivity and oxygen solubility, and incorporate them into high surface area carbon black support. Further, we establish a correlation between the physical properties and electrochemical performance of the ionic liquid-modified catalysts by providing direct evidence of ionic liquids role in altering hydrophilic/hydrophobic interactions within the catalyst layer interface. The resulting catalyst with optimized interface design achieved a high mass activity of 347 A g−1Pt at 0.9 V under H2/O2, power density of 0.909 W cm−2 under H2/air and 1.5 bar, and had only 0.11 V potential decrease at 0.8 A cm−2 after 30 k accelerated stress test cycles. This performance stems from substantial enhancement in Pt utilization, which is buried inside the mesopores and is now accessible due to ILs addition.

No abstract

No abstract

Multiwalled carbon nanotubes (MWCNTs) were modified by an organo-silane in order to improve their dispersion state and stability in paraffin wax. A family of paraffin-based phase change material (PCM) composites filled with MWCNTs was prepared with different loadings (0, 0.1, 0.5, and 1 wt%) of pristine MWCNTs and organo-silane modified MWCNTs (Si-MWCNT). Structural analyses were performed by means of Fourier transform infrared (FTIR), scanning electron microscopy (SEM), and rheological studies using temperature sweeps. Moreover, phase change transition temperatures and heat of fusion as well as thermal and electrical conductivities of the developed PCM nanocomposites were determined. The SEM micrographs and FTIR absorption bands appearing at approximately 1038 and 1112 cm −1 confirmed the silane modification. Differential scanning calorimetery (DSC) results indicate that the presence of Si-MWCNTs leads to slightly favorable enhancement in the energy storage capacity at the maximum loading. It was also shown that the thermal conductivity of the PCM nanocomposites, in both solid and liquid phases, increased with increasing the MWCNT content independent of the kind of MWCNTs by up to about 30% at the maximum loading of MWCNTs. In addition, the modification of MWCNTs made the samples completely electrically nonconductive, and the electrical surface resistivity of the PCMs containing pristine MWCNTs decreased with increasing MWCNTs loading. Furthermore, the rheological assessment under consecutive cyclic phase change demonstrated that the samples containing modified MWCNTs are more stable compared to the PCM containing pristine MWCNTs.

The reactive compatibilization of blends consisting polypropylene (PP) and thermoplastic starch (TPS) (70/30) with different portions of PP‐grafted maleic anhydride (PP‐g‐MA) is carried out by melt mixing. The esterification reaction between the starch hydroxyl and the PP‐g‐MA groups proved by the FTIR leads to a compatibility improvement. The dynamic rheological properties, morphology, elongation at break, and the impact strength of the blends were studied. The SEM images show that increasing the compatibilizer concentration reduces the dispersed TPS droplet size. The generalized Zener model states that an elastic interface is established (minimum α value) and enables us to predict the dynamic rheological properties of our blends in a longer frequency range to where the current experimental limitation exists. The modified Cross model is implemented to confirm better adhesion between phases when 20 wt % PP‐g‐MA is used (minimum ac value). The increase in the dynamic viscoelastic moduli at concentrations up to 20 wt % and the observed plateau at the elongation at break point at this concentration confirmed that this concentration is the optimum for the maximum stress transfer. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2020, 137, 48742.