No abstract

We have performed a study of the magnetic, magnetoelastic, and corrosion resistance properties of seven different composition magnetoelastic-resonant platforms. For some applications, such as structural health monitoring, these materials must have not only good magnetomechanical properties, but also a high corrosion resistance. In the fabricated metallic glasses of composition 73− 5 10 12 , the Fe/Ni ratio was varied (Fe + Ni = 73% at. ) thus changing the magnetic and magnetoelastic properties. A small amount of chromium (Cr 5 ) was added in order to achieve the desired good corrosion resistance. As expected, all the studied properties change with the composition of the samples. Alloys containing a higher amount of Ni than Fe do not show magnetic behavior at room temperature, while iron-rich alloys have demonstrated not only good magnetic properties, but also good magnetoelastic ones, with magnetoelastic coupling coefficient as high as 0.41 for = 0 in the 73 0 5 10 12 (the sample containing only Fe but not Ni ). Concerning corrosion resistance, we have found a continuous degradation of these properties as the Ni content increases in the composition. Thus, the corrosion potential decreases monotonously from 46.74 mV for the = 0, composition 73 0 5 10 12 to −239.47 mV for the = 73, composition 0 73 5 10 12 .

In the present work, a nanostructured ZnO layer was synthesized onto a Metglas magnetoelastic ribbon to immobilize hemoglobin (Hb) on it and study the Hb’s electrochemical behavior towards hydrogen peroxide. Hb oxidation by H2O2 was monitored simultaneously by two different techniques: Cyclic Voltammetry (CV) and Magnetoelastic Resonance (MR). The Metglas/ZnO/Hb system was simultaneously used as a working electrode for the CV scans and as a magnetoelastic sensor excited by external coils, which drive it to resonance and interrogate it. The ZnO nanoparticles for the ZnO layer were grown hydrothermally and fully characterized by X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM) and photoluminescence (PL). Additionally, the ZnO layer’s elastic modulus was measured using a new method, which makes use of the Metglas substrate. For the detection experiments, the electrochemical cell was performed with a glass vial, where the three electrodes (working, counter and reference) were immersed into PBS (Phosphate Buffer Solution) solution and small H2O2 drops were added, one at a time. CV scans were taken every 30 s and 5 min after the addition of each drop and meanwhile a magnetoelastic measurement was taken by the external coils. The CV plots reveal direct electrochemical behavior of Hb and display good electrocatalytic response to the reduction of H2O2. The measured catalysis currents increase linearly with the H2O2 concentration in a wide range of 25–350 μM with a correlation coefficient 0.99. The detection limit is 25–50 μM. Moreover, the Metglas/ZnO/Hb electrode displays rapid response (30 s) to H2O2, and exhibits good stability and reproducibility of the measurements. On the other hand, the magnetoelastic measurements show a small linear mass increase versus the H2O2 concentration with a slope of 152 ng/μM, which is probably due to H2O2 adsorption in ZnO during the electrochemical reaction. No such effects were detected during the control experiment when only PBS solution was present for a long time.

The main parameters of magnetoelastic resonators in the detection of chemical (i.e., salts, gases, etc.) or biological (i.e., bacteria, phages, etc.) agents are the sensitivity S (or external agent change magnitude per Hz change in the resonance frequency) and the quality factor Q of the resonance. We present an extensive study on the experimental determination of the Q factor in such magnetoelastic resonant platforms, using three different strategies: (a) analyzing the real and imaginary components of the susceptibility at resonance; (b) numerical fitting of the modulus of the susceptibility; (c) using an exact mathematical expression for the real part of the susceptibility. Q values obtained by the three methods are analyzed and discussed, aiming to establish the most adequate one to accurately determine the quality factor of the magnetoelastic resonance.