Polymerization behavior of N-phenylbenzoxazine in bulk was studies in detail to discover new reaction pathways: (1) formation of an intermediary polymer having N,O-acetal-type linkage in the main chain and (2) its rearrangement into Mannich-type linkage in the solid state. Efficient promotion of the main chain rearrangement was achieved by using a dual system composed of imidazole and sulfonic acid.

No abstract

Thermally induced polymerizations of a series of 1,3‐benzoxazines with a variety of substituents on the nitrogen atom were investigated in detail, particularly in the following three aspects of the polymerization: (1) N‐alkyl‐1,3‐benzoxazines are much more reactive than N‐phenyl‐1,3‐benzoxazine. (2) The polymerization rate depended on the bulkiness of the N‐substituent. The bulkier the substituent was, the slower the polymerization was. (3) The polymerizations accompanied weight loss due to the elimination of the corresponding imine (R‐N = CH2), and its extent became larger when R was more bulky. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 2777–2782, 2010

The click‐coupling reaction was applied to polycondensation, to synthesize a high‐molecular weight prepolymer having benzoxazine moieties in the main chain. For the polycondensation, a bifunctional N‐propargyl benzoxazine was synthesized from bisphenol A, propargylamine, and formaldehyde. The propargyl group was efficiently used for the copper(I)‐catalyzed alkyne‐azide “click” reaction with p‐xylene‐α,α′‐diazide, to give the corresponding linear polycondensate having 1,2,3‐triazole junctions. The polycondensation proceeded in N,N‐dimethylformamide (DMF) at room temperature. By this highly efficient “click‐” polycondensation reaction, the benzoxazine ring in the monomer was successfully introduced into the polymer main chain without any side reaction. The obtained polymer (=prepolymer) underwent thermal crosslinking to afford the corresponding product, which was insoluble in a wide range of organic solvents and exhibited higher thermal stability than the polymer before crosslinking. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 2316–2325, 2008