This study investigated the solubility of mineral trioxide aggregate (MTA) and Portland cement since its mixture until 672 hours, by means of two complimentary methods. Metal ring molds filled with the cements were covered with distilled water and, at each experimental time (3, 24, 72, 168, 336 and 672 hours), were weighed as soon as the plates in which the samples have been placed. Empty rings served as the control group (n=8). Mean weight gain and loss was determined and analyzed statistically by two-way ANOVA and Tukey's test for all pairwise comparisons. Only Portland cement showed less than 3% weight loss through 24 hours. Detached MTA residues were heavier than those of Portland cement over the 3 to 168 hours. The weight of MTA rings increased more than that of Portland rings within 672 hours (p=0.05). The findings of the present study indicate that, in an aqueous environment MTA is more soluble than Portland cement and exceeds the maximum weight loss considered acceptable by ISO 6876 standard (2001).

The objective of this study was to evaluate the long-term influence of xenogenic grafts on bone crestal height and radiographic density following extraction of teeth. The right and left third lower molars of 22 patients were surgically extracted, and one randomly chosen socket was filled with a xenogenic graft (Gent-Tech). The contralateral molar was left to heal naturally, serving as a paired control. Digital intraoral radiographies were taken at surgery and 2, 6, and 24 months after, to evaluate bone density (BD) and alveolar bone crest to cementoenamel junction distance. The data obtained were subjected to two-way analysis of variance and Tukey's test (α = 0.05). The significant decrease in cementoenamel junction distance observed for both groups was limited to the first 6 months. BD values increased significantly in the first 6 months, with no alterations observed up to 24 months for both groups. BD was higher for the experimental group at all time points (p < 0.05). Socket grafting with the xenogenic materials tested did not changed bone crestal height and bone radiographic density in the long term.

The aim of this study was to investigate whether a final rinse with Endosolv R ® solvent and ultrasound resulted in cleaner root canal walls during endodontic retreatment. A total of 56 extracted premolar teeth were manually instrumented using a step-back flare technique and filled with gutta-percha and AH Plus sealer. After 9 months, the canals were retreated by removing the gutta-percha and sealer with ProTaper Universal Retreatment and rotary preparation with ProTaper Universal System up to an F5 file. As a final step, the teeth were randomly divided in 4 groups (n=14) and were subjected to passive ultrasonic irrigation (PUI) with either Endosolv R or distilled water. In the control groups, the irrigants were left undisturbed. Roots were cleaved and examined under scanning electron microscopy (SEM), and the amount of filling remnants on the canal walls was assessed by two calibrated examiners in a blinded fashion. Data were analyzed by the Kruskal-Wallis test and the Student-Newman-Keuls post hoc test (α=0.05). All groups presented filling debris in the three root canal thirds after retreatment. There were no significant differences between the groups or among the root canal thirds within each group (p>0.05). PUI with Endosolv R was not effective in the removal of filling debris from root canal walls.

The aim of this study was to evaluate the effects of different irrigants on sealer-dentin bond strength when using Real Seal. Thirty single-rooted teeth were divided into 3 groups. In one group, the teeth were irrigated with 3 mL of 2.5% NaOCl after each file change, flushed with 17% EDTA for 3 min and finally rinsed with 3 mL of 2.5% NaOCl. In the other two groups, rinse with NaOCl was replaced with 2% chlorhexidine gluconate (CHX) and 0.9% saline, respectively. Each root was sectioned transversally into apical, middle and coronal thirds to obtain 2-mm-thick slices. Each slice was filled with Real Seal and Resilon. Push-out test was used to analyze bond strength and failure modes were classified as adhesive, cohesive or mixed, according to SEM observations. The push-out test did not reveal any statistically significant difference (p>0.05) between the irrigants. However, the groups exhibited significantly different (p<0.05) bond strengths in terms of the root canal third. Higher bond strength was observed at the apical third when compared with coronal third, while middle third presented intermediary values. Fifteen specimens were analyzed by SEM (5 per group). Eleven specimens exhibited adhesive failures (5 in saline, 4 in NaOCl and 2 in CHX group); 2 cohesive failures were observed in the CHX group, and 1 mixed failure each was observed in the CHX and NaOCl groups. The tested irrigants did not influence the bond strength of Resilon and Real Seal to dentin. The apical third exhibited higher mean bond strengths and adhesive failures were predominant.

Objectives:This clinical study evaluated the effects of a highly concentrated home-bleaching agent on the surface morphology of aesthetically restored teeth.Methods:Specimens of human enamel and micro-hybrid composite resin were randomly adhered to the buccal side of right premolar and molar teeth of ten volunteers, who underwent a routine home-bleaching procedure with 16% carbamide peroxide on the upper jaw for 8 days. The mandibular unbleached specimens served as paired controls (n=10). Ultra-structural assessment of the sample was carried out by scanning electron microscopy, and the resulting images were blindly evaluated for topographical alterations. The differences between groups were calculated with the Mann-Whitney test adjusted at the 95% confidence interval.Results:The bleached enamel presented significantly more morphological changes than the control group. The aspect of resin composite exposed to the whitening substance was statistically similar to that observed in the corresponding control group (P<.05).Conclusions:The occurrence of surface topography changes during home bleaching of aesthetically restored teeth with 16% carbamide peroxide was restricted to enamel.