In this study, the corrosion mechanisms of the AA2024-T3 and the AA2098-T351 were investigated and compared using various electrochemical techniques in 0.005 mol L −1 NaCl solution. The severe type of corrosion in the AA2098-T351 was intragranular attack (IGA) although trenching and pitting related to the constituent particles were seen. On the other hand, the AA2024-T3 exhibited severe localised corrosion associated with micrometric constituent particles, and its propagation was via grain boundaries leading to intergranular corrosion (IGC). Electrochemical techniques showed that the corrosion reaction in both alloys was controlled by diffusion. The non-uniform current distribution in both alloys showed that EIS was not a proper technique for comparing the corrosion resistance of the alloys. However, local electrochemical techniques were useful for the evaluation of the corrosion resistance of the alloys.

HAL is a multidisciplinary open access archive for the deposit and dissemination of scientific research documents, whether they are published or not. The documents may come from teaching and research institutions in France or abroad, or from public or private research centers. L'archive ouverte pluridisciplinaire HAL, est destinée au dépôt et à la diffusion de documents scientifiques de niveau recherche, publiés ou non, émanant des établissements d'enseignement et de recherche français ou étrangers, des laboratoires publics ou privés.

No abstract

No abstract