The biodegradable PLGA and PCL electro-spun scaffolds resulted in equal biocompatibility, while PMMA showed cytotoxicity. Only PLGA preserved hCEC morphology and consequently seems to be a promising candidate for TEEG construction.

This paper describes a magnetic nanotechnology that locally enables hyperthermia treatment of hollow organ tumors by using polymer hybrid stents with incorporated magnetic nanoparticles (MNP). The hybrid stents are implanted and activated in an alternating magnetic field to generate therapeutically effective heat, thereby destroying the tumor. Here, we demonstrate the feasibility of nanomagnetic actuation of three prototype hybrid stents for hyperthermia treatment of hollow organ tumors. The results show that the heating efficiency of stent filaments increases with frequency from approximately 60 W/gFe (95 kHz) to approximately 250 W/gFe (270 kHz). The same trend is observed for the variation of magnetic field amplitude; however, heating efficiency saturates at approximately 30 kA/m. MNP immobilization strongly influences heating efficiency showing a relative difference in heating output of up to 60% compared to that of freely dispersed MNP. The stents showed uniformly distributed heat on their surface reaching therapeutically effective temperatures of 43 °C and were tested in an explanted pig bile duct for their biological safety. Nanomagnetic actuation of hybrid stents opens new possibilities in cancer treatment of hollow organ tumors.

Electro-spinning is widely used in tissue-engineered applications mostly in form of non-woven structures. The development of e-spun yarn opens the door for textile fabrics which combine the micro to nanoscale dimension of electro-spun filaments with three-dimensional (3D) drapable textile fabrics. Therefore, the aim of the study was the implementation of a process for electro-spun yarns. Polylactic acid (PLA) and polyethylene glycol (PEG) were spun from chloroform solutions with varying PLA/PEG ratios (100:0, 90:10, 75:25 and 50:50). The yarn samples produced were analyzed regarding their morphology, tensile strength, water uptake and cytocompatibility. It was found that the yarn diameter decreased when the funnel collector rotation was increasd, however, the fiber diameter was not influenced. The tensile strength was also found to be dependent on the PEG content. While samples composed of 100% PLA showed a tensile strength of 2.5±0.7 cN/tex, the tensile strength increased with a decreasing PLA content (PLA 75%/PEG 25%) to 6.2±0.5 cN/tex. The variation of the PEG content also influenced the viscosity of the spinning solutions. The investigation of the cytocompatibility with endothelial cells was conducted for PLA/PEG 90:10 and 75:25 and indicated that the samples are cytocompatible.

Tissue Engineering is considered a promising route to address existing deficits of autografts and permanent synthetic prostheses for tendons and ligaments. However, the requirements placed on the scaffold material are manifold and include mechanical, biological and degradation-related aspects. In addition, scalable processes and FDA-approved materials should be applied to ensure the transfer into clinical practice. To accommodate these aspects, this work focuses on the high-scale fabrication of high-strength and highly oriented polycaprolactone (PCL) fibers with adjustable cross-sectional geometry and degradation kinetics applying melt spinning technology. Four different fiber cross-sections were investigated to account for potential functionalization and cell growth guidance. Mechanical properties and crystallinity were studied for a 24-week exposure to phosphate-buffered saline (PBS) at 37 °C. PCL fibers were further processed into scaffolds using multistage circular braiding with three different hierarchical structures. One structure was selected based on its morphology and scaled up in thickness to match the requirements for a human anterior cruciate ligament (ACL) replacement. Applying a broad range of draw ratios (up to DR9.25), high-strength PCL fibers with excellent tensile strength (up to 69 cN/tex) could be readily fabricated. The strength retention after 24 weeks in PBS at 37 °C was 83–93%. The following braiding procedure did not affect the scaffolds’ mechanical properties as long as the number of filaments and the braiding angle remained constant. Up-scaled PCL scaffolds resisted loads of up to 4353.88 ± 37.30 N, whilst matching the stiffness of the human ACL (111–396 N/mm). In conclusion, this work demonstrates the fabrication of highly oriented PCL fibers with excellent mechanical properties. The created fibers represent a promising building block that can be further processed into versatile textile implants for tissue engineering and regenerative medicine.