No abstract

Resonance frequency (RF) analysis is a non-invasive, objective and sensitive technique developed for implantology where it measures the stability of the implant in osteotomy site. Although many studies were performed by the previous electronic version of RF analyzer, a very limited number of studies were carried out with the new magnetic wireless version. The aim of the study was to evaluate the relation between insertion torques, primary and secondary stability of self-tapping tapered implant systems. Thirteen subjects were treated with 42 endosseous implants using two-stage surgical procedure. The maximal insertion torque values were recorded prior to RF analysis during surgery. Six months after surgery, the secondary stability values were measured by the RF analysis. The average maximal insertion torque and primary and secondary magnetic RF values were 33 +/- 11 N cm and 66 +/- 12 ISQ and 71.9 +/- 6 ISQ for 42 implants respectively. The correlation between insertion torque and RF values were indicated to be statistically significant (P < 0.01). Significantly higher maximal insertion torque, and primary and secondary magnetic RF values were achieved in mandibular sites compared with maxillary areas (P < 0.01). No significant differences were measured for all parameters when both systems were compared with each other (P > 0.05). There was a strong correlation between the insertion torque, primary and secondary magnetic RF values of self-tapping tapered endosseous implant used. Further studies are needed to understand the impact of the wireless magnetic RF analysis technique in clinics.

PURPOSEThe purpose of this study was to assess the effect of surface treatments on shear bond strength of resin composite bonded to thermocycled and non-thermocycled CAD/CAM resin-ceramic hybrid materials.MATERIALS AND METHODS120 specimens (10×10×2 mm) from each material were divided into 12 groups according to different surface treatments in combination with thermal aging procedures. Surface treatment methods were airborne-particle abrasion (abraded with 50 micron alumina particles), dry grinding (grinded with 125 µm grain size bur), and hydrofluoric acid (9%) and silane application. According to the thermocycling procedure, the groups were assigned as non-thermocycled, thermocycled after packing composites, and thermocycled before packing composites. The average surface roughness of the non-thermocycled specimens were measured after surface treatments. After packing composites and thermocycling procedures, shear bond strength (SBS) of the specimens were tested. The results of surface roughness were statistically analyzed by 2-way Analysis of Variance (ANOVA), and SBS results were statistically analyzed by 3-way ANOVA.RESULTSSurface roughness of GC were significantly lower than that of LU and VE (P<.05). The highest surface roughness was observed for dry grinding group, followed by airborne particle abraded group (P<.05). Comparing the materials within the same surface treatment method revealed that untreated surfaces generally showed lower SBS values. The values of untreated LU specimens showed significantly different SBS values compared to those of other surface treatment groups (P<.05).CONCLUSIONSBS was affected by surface treatments. Thermocycling did not have any effect on the SBS of the materials except acid and silane applied GC specimens, which were subjected to thermocycling before packing of the composite resin.

No abstract

No abstract