Abstract:The poor patency rate following small-diameter vascular grafting remains a major hurdle for the widespread clinical application of artificial blood vessels to date. Our previous studies found that electrospun poly(L-lactide-co-epsilon-caprolactone) (P[LLA-CL]) nanofibers facilitated the attachment and growth of endothelial cells (EC), and heparin incorporated into P(LLA-CL) nanofibers was able to release in a controlled manner. Hence, we hypothesized that heparin-bonded P(LLA-CL) vascular scaffolds with autologous EC pre-endothelialization could significantly promote the graft patency rate. To construct a small-diameter vascular scaffold, the inner layer was fabricated by heparin-bonded P(LLA-CL) nanofibers through coaxial electrospinning, while the outer layer was woven by pure P(LLA-CL) nanofibers. Except dynamic compliance (5.4 ± 1.7 versus 12.8 ± 2.4 × 10 −4 /mmHg, P , 0.05), maximal tensile strength, burst pressure, and suture retention of the composite, scaffolds were comparable to those of canine femoral arteries. In vitro studies indicated that the scaffolds can continuously release heparin for at least 12 weeks and obtain desirable endothelialization through dynamic incubation, which was confirmed by EC viability and proliferation assay and scanning electronic microscopy. Furthermore, in vivo studies demonstrated that pre-endothelialization by autologous ECs provided a better effect on graft patency rate in comparison with heparin loading, and the united application of pre-endothelialization and heparin loading markedly promoted the 24 weeks patency rate of P(LLA-CL) scaffolds (88.9% versus 12.5% in the control group, P , 0.05) in the canine femoral artery replacement model. These results suggest that heparin-bonded P(LLA-CL) scaffolds have similar biomechanical properties to those of native arteries and possess a multiporous and biocompatible surface to achieve satisfactory endothelialization in vitro. Heparin-bonded P(LLA-CL) scaffolds with autologous EC pre-endothelialization have the potential to be substitutes for natural small-diameter vessels in planned vascular bypass surgery.

A biomaterial patch of electrospun collagen type fibers was designed and produced by electrospinning seven different concentrations (8%-20% w/v) of collagen solutions. The tensile strength, yield strength, and elastic modulus of the electrospun collagen fibrous patches were found to be suitable for clinical transplantation. No significant differences versus fresh porcine pericardium as controls were observed. The SEM images of the groups showed that the patches were smooth with uniform interwoven and porous morphology. The fibrous patches were biocompatible and did not elicit local or systemic toxic effects when implanted in vivo. These electrospun collagen fibrous patches have significant potential as surgical biomaterial patches.