The rechargeable aqueous Zn ion battery (ZIB) is a promising candidate for next-generation energy storage technology due to its low cost, low flammability, inherent safety, and high theoretical capacity. Nevertheless,...

In this study, mesoporous WO films with oxygen vacancy defects have been fabricated using the camphene-assisted sol-gel method. By controlling the optimized weight ratio of camphene on the WO films, we developed a unique film structure of the WO phase with both mesoporous morphology and oxygen vacancy defects due to the distinctive effect of camphene. The mesoporous WO films with oxygen vacancy defects fabricated using 10 wt% camphene showed superb multifunctional electrochromic (EC) properties with both fast switching speeds (5.8 s for coloration speed and 1.0 s for bleaching speed) and high coloration efficiency (CE, 51.4 cm C), which include the most prominent properties, particularly for switching speeds among WO-based films reported so far. The attractive EC properties are due to the synergistic effects of the mesoporous morphology and oxygen vacancy defects on the WO. The fast switching speeds are mainly caused by the reduced Li diffusion pathway due to the mesoporous morphology and increased electrical conductivity due to the oxygen vacancy defects. In addition, the increased CE value is due to the large transmittance modulation as a result of a more effective electrostatic contact of the mesoporous morphology and an increased optical bandgap of the oxygen vacancy defects on the WO. Therefore, this unique film structure of the mesoporous WO films with oxygen vacancy defects can be potentially regarded as a novel EC material for high-performance EC devices.