Scanning electron microscopy, linear sweep voltammetry, chronoamperometry, and in situ surface-enhanced Raman spectroscopy were used to investigate the electrochemical oxygen evolution reaction (OER) occurring on cobalt oxide films deposited on Au and other metal substrates. All experiments were carried out in 0.1 M KOH. A remarkable finding is that the turnover frequency for the OER exhibited by ∼0.4 ML of cobalt oxide deposited on Au is 40 times higher than that of bulk cobalt oxide. The activity of small amounts of cobalt oxide deposited on Pt, Pd, Cu, and Co decreased monotonically in the order Au > Pt > Pd > Cu > Co, paralleling the decreasing electronegativity of the substrate metal. Another notable finding is that the OER turnover frequency for ∼0.4 ML of cobalt oxide deposited on Au is nearly three times higher than that for bulk Ir. Raman spectroscopy revealed that the as-deposited cobalt oxide is present as Co(3)O(4) but undergoes progressive oxidation to CoO(OH) with increasing anodic potential. The higher OER activity of cobalt oxide deposited on Au is attributed to an increase in fraction of the Co sites present as Co(IV) cations, a state of cobalt believed to be essential for OER to occur. A hypothesis for how Co(IV) cations contribute to OER is proposed and discussed.

The selective electroreduction of carbon dioxide to C2 compounds (ethylene and ethanol) on copper­(I) oxide films has been investigated at various electrochemical potentials. Aqueous 0.1 M KHCO3 was used as electrolyte. A remarkable finding is that the faradic yields of ethylene and ethanol can be systematically tuned by changing the thickness of the deposited overlayers. Films 1.7–3.6 μm thick exhibited the best selectivity for these C2 compounds at −0.99 V vs RHE, with faradic efficiencies (FE) of 34–39% for ethylene and 9–16% for ethanol. Less than 1% methane was formed. A high C2H4/CH4 products’ ratio of up to ∼100 could be achieved. Scanning electron microscopy, X-ray diffraction, and in situ Raman spectroscopy revealed that the Cu2O films reduced rapidly and remained as metallic Cu0 particles during the CO2 reduction. The selectivity trends exhibited by the catalysts during CO2 reduction in phosphate buffer, and KHCO3 electrolytes suggest that an increase in local pH at the surface of the electrode is not the only factor in enhancing the formation of C2 products. An optimized surface population of edges and steps on the catalyst is also necessary to facilitate the dissociation of CO2 and the dimerization of the pertinent CH x O intermediates to ethylene and ethanol.

An in situ Raman spectroscopic investigation has been carried out to identify the composition of the active phase present on the surface of nickel electrodes used for the electrochemical evolution of oxygen. The electrolyte in all cases was 0.1 M KOH. A freshly polished Ni electrode oxidized upon immersion in the electrolyte and at potentials approaching the evolution of oxygen developed a layer of γ-NiOOH. Electrochemical cycling of this film transformed it into β-NiOOH, which was observed to be three times more active than γ-NiOOH. The higher activity of β-NiOOH is attributed to an unidentified Ni oxide formed at a potential above 0.52 V (vs Hg/HgO reference). We have also observed that a submonolayer of Ni oxide deposited on Au exhibits a turnover frequency (TOF) for oxygen evolution that is an order of magnitude higher than that for a freshly prepared γ-NiOOH surface and more than 2-fold higher than that for a β-NiOOH surface. By contrast, a similar film deposited on Pd exhibits a TOF that is similar to that of bulk γ-NiOOH. It is proposed that the high activity of submonolayer deposits of Ni oxide on Au is due to charge transfer from the oxide to the highly electronegative Au, leading to the possible formation of a mixed Ni/Au surface oxide.