The discovery of inverse vulcanization has allowed stable polymers to be made from elemental sulfur, an unwanted by-product of the petrochemicals industry. However, further development of both the chemistry and applications is handicapped by the restricted choice of cross-linkers and the elevated temperatures required for polymerisation. Here we report the catalysis of inverse vulcanization reactions. This catalytic method is effective for a wide range of crosslinkers reduces the required reaction temperature and reaction time, prevents harmful H2S production, increases yield, improves properties, and allows crosslinkers that would be otherwise unreactive to be used. Thus, inverse vulcanization becomes more widely applicable, efficient, eco-friendly and productive than the previous routes, not only broadening the fundamental chemistry itself, but also opening the door for the industrialization and broad application of these fascinating materials.
Sulfur is an underused by-product of the petrochemicals industry.R ecent research into inverse vulcanization has shown how this excesss ulfur can be transformed into functional polymers, by stabilization with organic crosslinkers. For these interesting new materials to realize their potential for applications,m ore understanding and control of their physical properties is needed. Here we report four new terpolymers prepared from sulfur and two distinct alkene monomers that can be predictively tuned in glass transition, molecular weight, solubility,m echanical properties, and color.
The invention of inverse vulcanization provides great opportunities for generating functional polymers directly from elemental sulfur, an industrial by‐product. However, unsatisfactory mechanical properties have limited the scope for wider applications of these exciting materials. Here, we report an effective synthesis method that significantly improves mechanical properties of sulfur‐polymers and allows control of performance. A linear pre‐polymer containing hydroxyl functional group was produced, which could be stored at room temperature for long periods of time. This pre‐polymer was then further crosslinked by difunctional isocyanate secondary crosslinker. By adjusting the molar ratio of crosslinking functional groups, the tensile strength was controlled, ranging from 0.14±0.01 MPa to 20.17±2.18 MPa, and strain was varied from 11.85±0.88 % to 51.20±5.75 %. Control of hardness, flexibility, solubility and function of the material were also demonstrated. We were able to produce materials with suitable combination of flexibility and strength, with excellent shape memory function. Combined with the unique dynamic property of S−S bonds, these polymer networks have an attractive, vitrimer‐like ability for being reshaped and recycled, despite their crosslinked structures. This new synthesis method could open the door for wider applications of sustainable sulfur‐polymers.
The reaction between sulfur and dicyclopentadiene was optimised to form a shelf stable and soluble low molecular weight oligomer. After a simple curing process at 140 °C the material was...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.