High-density polyethylene (HDPE) and nanosilica nanocomposites were prepared for SiO 2 content up to 15 wt%. Microstructural characterization evidenced a homogenous distribution of silica aggregates with a mean size increasing with the filler content finally resulting in a rheological percolation between 7.5 and 10 wt%. Nanoparticles did not induce any significant impact on the matrix crystallinity but led to a real improvement on elastic properties accompanied with a large embrittlement above the percolation threshold. The effect of annealing near HDPE melting temperature was studied. Differential scanning calorimetry, X-ray diffraction, and small-angle X-ray scattering analyses showed a significant change in the HDPE microstructure after annealing at 125 C. A large increase in the crystallinity (from 68 to 76%) and a clear improvement of Young's modulus (by 55%) were observed prior to polymer degradation. A valuable impact of silica particles on thermal stability was also obvious regarding the evolution of elastic properties for extended exposure times (850-1,200 h).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.