The electrochemical behavior of Ti3+ in LiCl-LiF-TiF3 salt was investigated by cyclic and square wave voltammetries at 853 K. Both methods confirm the presence of a single reduction wave of Ti3+ ions to metal, at a potential of −2.3 V vs. Cl2/Cl−. The closeness of the potentials of TiCxOy dissolution and Ti3+/Ti4+ wave is an issue during the electrorefining of the anode. A low current density has to be applied to stay within the titanium oxycarbide dissolution and avoid the formation of Ti4+. The titanium deposition was studied by electrorefining of a titanium metal plate in LiCl-LiF-TiF3 (0.62 mol/kg). The cathodic deposit analysis by XRD and SEM confirms the formation of titanium metal with an average grain size of 150 µm. The faradic deposition yields are above 85% and constant between 60 and 160 mA/cm2.