Debonding at the composite-adhesive interface is a major problem for indirect composite restorations. The aim of this study was to evaluate the bond strength (BS) of an indirect composite resin after various surface treatments (air-abrasion with Al2O3, phosphoric acid-etchig and different applications of NdYAG laser irradiations). Fifty composite disks were subjected to secondary curing to complete polymerization and randomly divided into five experimental groups (n = 10) including Group 1, untreated (control); Group 2, phosphoric acid-etched; Group 3, air-abrasion with Al2 O3 ; Group 4, Nd:YAG laser irradiated with non-contact and Group 5, Nd:YAG laser irradiated with contact. They were then bonded to resin cement and shear BS was determined in a universal testing device at a crosshead speed of 1 mm/min. One way analysis of variance (ANOVA) and Tukey post-hoc tests were used to analyze the BS values. The highest BS value was observed in Group 4 and followed by Group 3. Tukey test showed that there was no statistical difference between Group1, 2 and 5. Furthermore, differences in BSs between Group 4 and the other groups except Group 3 were significant (p < 0.05) and also there were significant differences in BSs between Group 3 to 1 and Group 3 to 2 (p < 0.05). This study reveals that air-abrasion with Al2 O3 and Nd:YAG laser irradiation with non-contact provided a significant increase in BS between indirect composite and resin cement.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.