No abstract

This paper studied the strengthening effects of silica nanoparticles on the polyacrylamide (PAM)/hydroquinone (HQ)–hexamethylenetetramine (HMTA) composite gel. Pure PAM/HQ–HMTA gel and PAM/HQ–HMTA gels containing silica nanoparticles up to 0.3 wt % were prepared at 110 °C. Influences of silica nanoparticles on gelation performances were systematically evaluated. By the addition of silica nanoparticles, the gelation time became shorter and the gel strength was improved observably. Rheological measurements showed that silica nanoparticles enhanced both elasticity and viscosity of the gel significantly. Thermal stability of the gel was studied by differential scanning calorimetry (DSC) measurements. The maximum tolerated temperature of the gel was improved from 137.8 to 155.5 °C by the addition of silica nanoparticles with a concentration of 0.3 wt %. Furthermore, to study the strengthening mechanisms of silica nanoparticles to the gel, the microstructure and existing state of water within the gel were investigated by environmental scanning electron microscopy (ESEM) and DSC measurements. Micrographs of the gel showed that massive aggregations and arrangements of silica nanoparticles existed in uniformly distributed three-dimensional network structures of the gel, which greatly improved the structural strength of the gel. Moreover, the mass fraction of bound water within the gel increased from 22.5 to 39.9% by the addition of silica nanoparticles with a concentration of 0.3 wt %. The hydrogen bonds and electrostatic attractions between silica nanoparticles and water molecules/hydronium ions make a higher bound water ratio, which contributes to better water holding capacity and thermal stability of the gel.

A new kind of self-dispersing silica nanoparticle was prepared and used to enhance oil recovery in spontaneous imbibition tests of low-permeability cores. To avoid the aggregation of silica nanoparticles, a new kind of silica nanoparticle was prepared through the surface modification with vinyltriethoxysilane and 2-mercaptobenzimidazole as modified agents. Transmission electron microscopy, Fourier transform infrared spectroscopy, dynamic light scattering, and ζ potential measurements were employed to characterize the modified silica nanoparticles. Dispersing experiments indicated that modified silica nanoparticles had superior dispersity and stability in alkaline water. To evaluate the performance of silica nanofluids for enhanced oil recovery compared to pH 10 alkaline water and 5 wt % NaCl solution, spontaneous imbibition tests in sandstone cores were conducted. The results indicated that silica nanofluids can evidently improve oil recovery. To investigate the mechanism of nanoparticles for enhanced oil recovery, the contact angle and interfacial tension were measured. The results showed that the adsorption of silica nanoparticles can change the surface wettability from oil-wet to water-wet and silica nanoparticles showed a little influence on oil/water interfacial tension. In addition, the change of the oil droplet shape on the hydrophobic surface was monitored through dynamic contact angle measurement. It was shown that silica nanoparticles can gradually detach the oil droplet from the hydrophobic surface, which is consistent with the structural disjoining pressure mechanism.

No abstract

No abstract