This paper reports a comparative case study on the use of different softening products for bed linen fabrics, specifically regarding the sewability of the fabrics. The market offers a wide variety of commercial formulations of softeners for this purpose, but the composition and price varies considerably. This work was aimed to assess the relationship between the cost and effectiveness of different softener formulations in home textiles finishing. Objectively, the effect of different softeners and their concentrations on sewability of the fabrics was studied. Non-ionic polyethylene dispersions and a cationic silicone softener microemulsion in different concentrations and combinations were considered in this investigation. It was found that a combination of silicone and polyethylene based softeners presents the most interesting cost/performance behavior.

In this work we focus on the optimization and thermal stability of nanocomposite TiAlN/Mo multilayers that were produced by reactive magnetron sputtering on high-speed steel substrates, with modulation periods below 5 nm. These multilayers were annealed between 600-900 8C for 1 h in a vacuum furnace. Preliminary X-ray results reveal that these coatings are very stable up to 900 8C, since the multilayer chemical modulation is not severely affected. At intermediate annealing temperatures the modulation period decreases due to interdiffusion at the interface, resulting in a thicker interface between metal/nitride and hence decreasing the thickness of those layers. D