Catheter associated urinary tract infections are common during hospitalization due to the formation of bacterial biofilms on the indwelling device. In this study, we report an innovative biotechnology-based approach for the covalent functionalization of silicone catheters with antifouling zwitterionic moieties to prevent biofilm formation. Our approach combines the potential bioactivity of a natural phenolics layer biocatalytically conjugated to sulfobetaine-acrylic residues in an enzymatically initiated surface radical polymerization with laccase. To ensure sufficient coating stability in urine, the silicone catheter is plasma-activated. In contrast to industrial chemical methods, the methacrylate-containing zwitterionic monomers are polymerized at pH 5 and 50 °C using as an initiator the phenoxy radicals solely generated by laccase on the phenolics-coated catheter surface. The coated catheters are characterized by X-ray photoelectron spectroscopy (XPS), Fourier transformed infrared (FTIR) analysis, atomic force microscopy (AFM), and colorimetrically. Contact angle and protein adsorption measurements, coupled with in vitro tests with the Gram-negative Pseudomonas aeruginosa and Gram-positive Staphylococcus aureus in static and dynamic conditions, mimicking the operational conditions to be faced by the catheters, demonstrate reduced biofilm formation by about 80% when compared to that of unmodified urinary catheters. The zwitterionic coating did not affect the viability of the human fibroblasts (BJ-5ta) over seven days, corresponding to the extended useful life of urinary catheters.

This work describes a novel enzymatic approach to develop a lignin-based adhesive aimed at replacing the synthetic latex in wool floor coverings. The adhesive production consisted of a lignin pre-activation step to oxidise it by a laccase-enhancer system followed by a phenolation step where natural phenolic compounds were copolymerised with lignin in order to increase its content of quinone structures reactive towards wool. The electrochemical behaviour of the adhesive precursors and the influence of process conditions on the adhesive characteristics suggested that the phenolic compounds were able to autopolymerise and copolymerise between themselves and with lignin during the enzymatic reaction. Consequently, the flexibility and bonding strength of the adhesive increased. The latter showed strength performance similar to that of the traditional latex-based adhesive. A satisfactory level of flexibility was obtained using polyethylene glycol as an external plasticizer of lignin.

No abstract

This study presents a simple method to reproducibly obtain well-aligned vertical ZnO nanowire arrays on silicon oxide (SiOx) substrates using seed crystals made from a mixture of ammonium hydroxide (NH4OH) and zinc acetate (Zn(O2CCH3)2) solution. In comparison, high levels of OH(-) concentration obtained using NaOH or KOH solutions lead to incorporation of Na or K atoms into the seed crystals, destroying the c-axis alignment of the seeds and resulting in the growth of misaligned nanowires. The use of NH4OH eliminates the metallic impurities and ensures aligned nanowire growth in a wide range of OH(-) concentrations in the seed solution. The difference of crystalline orientations between NH4OH- and NaOH-based seeds is directly observed by lattice-resolved images and electron diffraction patterns using a transmission electron microscope (TEM). This study obviously suggests that metallic impurities incorporated into the ZnO nanocrystal seeds are one of the factors that generates the misaligned ZnO nanowires. This method also enables the use of silicon oxide substrates for the growth of vertically aligned nanowires, making ZnO nanostructures compatible with widely used silicon fabrication technology.

No abstract