Some photovoltaic module technologies use toxic materials. We report long-term leaching on photovoltaic module pieces of 5 × 5 cm2 size. The pieces are cut out from modules of the four major commercial photovoltaic technologies: crystalline and amorphous silicon, cadmium telluride as well as from copper indium gallium diselenide. To simulate different environmental conditions, leaching occurs at room temperature in three different water-based solutions with pH 3, 7, and 11. No agitation is performed to simulate more representative field conditions. After 360 days, about 1.4% of lead from crystalline silicon module pieces and 62% of cadmium from cadmium telluride module pieces are leached out in acidic solutions. The leaching depends heavily on the pH and the redox potential of the aqueous solutions and it increases with time. The leaching behavior is predictable by thermodynamic stability considerations. These predictions are in good agreement with the experimental results.

This study identifies unstable and soluble layers in commercial photovoltaic modules during 1.5 year long-term leaching. Our experiments cover modules from all major photovoltaic technologies containing solar cells from crystalline silicon (c-Si), amorphous silicon (a-Si), cadmium telluride (CdTe), and copper indium gallium diselenide (CIGS). These technologies cover more than 99.9% of the world market. We cut out module pieces of 5 × 5 cm2 in size from these modules and leached them in water-based solutions with pH 4, pH 7, and pH 11, in order to simulate different environmental conditions. Unstable layers open penetration paths for water-based solutions; finally, the leaching results in delamination. In CdTe containing module pieces, the CdTe itself and the back contact are unstable and highly soluble. In CIGS containing module pieces, all of the module layers are more or less soluble. In the case of c-Si module pieces, the cells’ aluminum back contact is unstable. Module pieces from a-Si technology also show a soluble back contact. Long-term leaching leads to delamination in all kinds of module pieces; delamination depends strongly on the pH value of the solutions. For low pH-values, the time dependent leaching is well described by an exponential saturation behavior and a leaching time constant. The time constant depends on the pH, as well as on accelerating conditions such as increased temperature and/or agitation. Our long-term experiments clearly demonstrate that it is possible to leach out all, or at least a large amount, of the (toxic) elements from the photovoltaic modules. It is therefore not sufficient to carry out experiments just over 24 h and to conclude on the stability and environmental impact of photovoltaic modules.

No abstract

Due to the toxicity of cadmium (Cd) and the scarcity of telluride (Te), CdTe-based photovoltaic modules have been under discussion during the last few years. In particular, the stability of CdTe in aqueous solutions is under debate. Here we show that the stability of CdTe depends not only on the pH of water-based solutions but also on size and surface treatment of CdTe particles. We compare milled module pieces with CdTe powders of different particle size. The leaching of CdTe is conditioned by the outdiffusion of Cd and Te at the interface between CdTe particles and the aqueous solution. The smaller the particle size, the faster the leaching. Therefore, milled module pieces decompose faster than CdTe powders with relatively large grains. We observe a dependence on time t according to t0.43. The room temperature diffusion coefficients are calculated as DCd ≈ 3 × 10−17 cm2/s for Cd, and DTe ≈ 1.5 × 10−17 cm2/s for Te in pH4. The chemical instability in aqueous solutions follows thermodynamic considerations. The solution behavior of Cd and Te depends on the pH value and the redox potential of the aqueous solutions. Chemical treatments such as those used in solar cell production modify the surface of the CdTe particles and their leaching behavior.