SynopsisStructural changes occurring during the fatigue failure of polyester fibers have been identified, and a comparison has been made with untested fibers and fibers which were subjected to cyclic loading conditions which did not produce fatigue. Fatigue failure was seen to result in a distinctive fracture morphology. Infrared spectrometry and X-ray diffraction revealed a lowering of crystallinity under fatigue conditions but not under other loading conditions. Transmission electron microscopy and electron diffraction revealed the creation of amorphous zones which are supposed as coalescing to form an amorphous band seen along and ahead of the fatigue crack. The zone just ahead of the fatigue crack tip is shown to contain voids. Crack propagation involves, therefore, the joining up of these voids and development along the amorphous band.