Brightening polymer-stabilized bistable cholesteric liquid crystal (PSBCLC) films with doped fluorescent dyes were prepared using the polymerization-induced phase separation (PIPS) method. The transmittance performance behavior of these films in both states (focal conic and planar) and absorbance change in multiple dye concentrations were studied using a UV/VIS/NIR spectrophotometer. The change occurring in dye dispersion morphology with different concentrations was obtained by means of the polarizing optical microscope. The maximum fluorescence intensity of different dye-doped PSBCLC films was measured using a fluorescence spectrophotometer. Moreover, the contrast ratios and driving voltages of these films were calculated and recorded to demonstrate film performance. Finally, the optimal concentration of dye-doped PSBCLC films with a high contrast ratio and a relatively low drive voltage was found. This is expected to have great potential applications in cholesteric liquid crystal reflective displays.

The SEM image of the polymer network of samples e1–e5: (e1) 4.8% C6M; (e2) 6.8% C6M; (e3) 8.8% C6M; (e4) 10.8% C6M; (e5) 12.8% C6M; and (e4′) cross-sectional image of e4.

No abstract

In this study, polymer-dispersed liquid crystal (PDLC) membranes were prepared by combining prepolymer, liquid crystal, and nanofiber mesh membranes under UV irradiation. EM, POM, and electro-optic curves were then used to examine the modified polymer network structure and the electro-optical properties of these samples. As a result, the PDLCs with a specific amount of reticular nanofiber films had considerably improved electro-optical characteristics and antiaging capabilities. The advancement of PDLC incorporated with reticulated nanofiber films, which exhibited a faster response time and superior electro-optical properties, would greatly enhance the technological application prospects of PDLC-based smart windows, displays, power storage, and flexible gadgets.

No abstract