Terpenoid cyclization reactions were observed in the course of reacting terpenes and sulfur to yield durable composites.

Herein are reported composites made by crosslinking unsaturated units in canola, sunflower or linseed oil with sulfur to yield CanS, SunS and LinS, respectively. These plant oils were selected because the average number of crosslinkable unsaturated units per triglyceride vary from 1.3 for canola to 1.5 for sunflower and 1.8 for linseed oil. The remeltable composites show compressive strengths that increase with increasing unsaturation number from CanS (9.3 MPa) to SunS (17.9 MPa) to LinS (22.9 MPa). These values for SunS and LinS are competitive when compared to the value of 17 MPa required for residential building using traditional Portland cement. The plant oil composites are recyclable over many cycles and can retain up to 100% of strength after 24 h in oxidizing acid under conditions where Portland cement is dissolved in under 30 min. Infusion of the composites into premade cement blocks affords them with significantly improved acid resistance as well. This work thus provides a simple, nearly 100% atom economical route to convert plant oils and waste sulfur to composites having enhanced performance over commercial structural materials.

A review with 132 references. Societal and regulatory pressures are pushing industry towards more sustainable energy sources, such as solar and wind power, while the growing popularity of portable cordless electronic devices continues. These trends necessitate the ability to store large amounts of power efficiently in rechargeable batteries that should also be affordable and long-lasting. Lithium-sulfur (Li-S) batteries have recently gained renewed interest for their potential low cost and high energy density, potentially over 2600 Wh kg−1. The current review will detail the most recent advances in early 2020. The focus will be on reports published since the last review on Li-S batteries. This review is meant to be helpful for beginners as well as useful for those doing research in the field, and will delineate some of the cutting-edge adaptations of many avenues that are being pursued to improve the performance and safety of Li-S batteries.

Terpenoids are potentially sustainable replacements for petrochemical olefins. Sulfur is a waste product produced in large quantities from fossil fuel refining. Several composites with attractive properties have recently been made from terpenoids and sulfur. This report details the extent to which the ratio of sulfur to terpenoid and the terpenoid olefin content influences the thermal and mechanical properties of such terpenoid-sulfur composites. The terpenoids selected were diunsaturated geraniol and triunsaturated farnesol that, upon their inverse vulcanization with elemental sulfur, yield composites GerSx and FarSx, respectively (x = wt % sulfur). The wt % sulfur in the monomer feed was varied from 30–95 for this study, providing twelve materials. Mechanical analysis of these materials was undertaken by compressive and tensile strength techniques. Differential scanning calorimetric analysis revealed both polymeric and orthorhombic sulfur present in the materials with glass transition temperatures (Tg) of −37 °C to −13 °C and melt temperatures (Tm) of 119 to 104 °C. The crystallinity of composites decreases as the weight fraction of sulfur decreases and composites having the highest olefin content exhibit no detectable crystalline microstructures. The compressive strength of the materials showed increasing strength for higher olefin-content materials for both GerSx (with compressive strength of up to 32 MPa) and FarSx (with compressive strength of up to 43 MPa). The improved strength with increasing olefin content levels off at around 80–85% of terpenoid, after which point both tensile and compressive strength diminish.