Thermoplastic vulcanized (TPV) nanocomposites were prepared in a laboratory mixer using EPDM, polypropylene of different viscosities, maleic anhydride modified polypropylene, an organo‐clay, and a sulfur‐based curing system. Based on the obtained results from X‐ray diffraction, transmission electron microscopy (TEM), scanning electron microscopy (SEM), differential scanning calorimeter, and mechanical properties, the microstructure of the prepared nanocomposites was found to be sensitive to the viscosity difference between the two phases and the clay content. X‐ray diffraction and TEM images of the TPV nanocomposites showed that clay was nearly exfoliated and randomly distributed into the polypropylene phase. The SEM photomicrographs of the dynamically vulcanized thermoplastic elastomer samples showed that the rubber particles were dispersed through the polypropylene in form of aggregates and their size increased with the introduction of clay. The nanoscale dimensions of the dispersed clay resulted in a significant improvement of the tensile modulus of the TPV nanocomposite samples, from 20 to 90% depending on clay content and the viscosity ratio of PP/EPDM. In the PP nanocomposites, the clay layers act as nucleating agents, resulting in higher crystallization temperature and reduced degree of crystallinity. Moreover, the oxygen permeability in the TPV nanocomposites was found to be lower than in unfilled but otherwise similar materials. POLYM. ENG. SCI., 47:207–217, 2007. © 2007 Society of Plastics Engineers.

No abstract

We report fabrication of a novel microstructured optical fiber made of biodegradable and water soluble materials that features approximately 1 dB/cm transmission loss. Two cellulose butyrate tubes separated with hydroxypropyl cellulose powder were codrawn into a porous double-core fiber offering integration of optical, microfluidic, and potentially drug release functionalities.

No abstract

We present the fabrication and use of plastic Photonic Band Gap Bragg fibers in photonic textiles for applications in interactive cloths, sensing fabrics, signage and art. In their cross section Bragg fibers feature periodic sequence of layers of two distinct plastics. Under ambient illumination the fibers appear colored due to optical interference in their microstructure. Importantly, no dyes or colorants are used in fabrication of such fibers, thus making the fibers resistant to color fading. Additionally, Bragg fibers guide light in the low refractive index core by photonic bandgap effect, while uniformly emitting a portion of guided color without the need of mechanical perturbations such as surface corrugation or microbending, thus making such fibers mechanically superior to the standard light emitting fibers. Intensity of side emission is controlled by varying the number of layers in a Bragg reflector. Under white light illumination, emitted color is very stable over time as it is defined by the fiber geometry rather than by spectral content of the light source. Moreover, Bragg fibers can be designed to reflect one color when side illuminated, and to emit another color while transmitting the light. By controlling the relative intensities of the ambient and guided light the overall fiber color can be varied, thus enabling passive color changing textiles. Additionally, by stretching a PBG Bragg fiber, its guided and reflected colors change proportionally to the amount of stretching, thus enabling visually interactive and sensing textiles responsive to the mechanical influence. Finally, we argue that plastic Bragg fibers offer economical solution demanded by textile applications.