In this study, a novel hemocompatible coating on stainless steel substrates was prepared by electrochemically copolymerizing 3,4-ethylenedioxythiophene (EDOT) with graphene oxide (GO), polystyrene sulfonate (PSS), or heparin (HEP) on SUS316L stainless steel, producing an anti-fouling (anti-protein adsorption and anti-platelet adhesion) surface to avoid the restenosis of blood vessels. The negative charges of GO, PSS, and HEP repel negatively charged proteins and platelets to achieve anti-fouling and anti-clotting. The results show that the anti-fouling capability of the poly(3,4-ethylenedioxythiophene) (PEDOT)/PSS coating is similar to that of the PEDOT/HEP coating. The anti-fouling capability of PEDOT/GO is higher than those of PEDOT/HEP and PEDOT/PSS. The reason for this is that GO exhibits negatively charged functional groups (COO−). The highest anti-fouling capability was found with the PEDOT/GO/HEP coating, indicating that electrochemical copolymerization of PEDOT with GO and HEP enhances the anti-fouling capability. Furthermore, the biocompatibility of the PEDOT coatings was tested with 3T3 cells for 1–5 days. The results show that all PEDOT composite coatings exhibited biocompatibility. The blood clotting time (APTT) of PEDOT/GO/HEP was prolonged to 225 s, much longer than the 40 s of pristine SUS316L stainless steel (the control), thus greatly improving the anti-blood-clotting capability of cardiovascular stents.

We have successfully fabricated poly(3,4-ethylenedioxythiophene) (PEDOT) derivative nanohybrid coatings on flexible SUS316L stainless steel by electrochemical polymerization, which can offer anti-fouling and anti-bacterial capabilities. PEDOT derivative nanohybrids were prepared from polystyrene sulfonates (PSS) and graphene oxide (GO) incorporated into a conducting polymer of PEDOT. Additionally, the negative charge of the PEDOT/GO substrate was further modified by poly-diallyldimethylammonium chloride (PDDA) to form a positively charged surface. These PEDOT derivative nanohybrid coatings could provide a straightforward means of controlling the surface energy, roughness, and charges with the addition of various derivatives in the electrochemical polymerization and electrostatically absorbed process. The characteristics of the PEDOT derivative nanohybrid coatings were evaluated by Raman spectroscopy, scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), water contact angle, and surface potential (zeta potential). The results show that PEDOT/PSS and PEDOT/GO nanohybrid coatings exhibit excellent anti-fouling capability. Only 0.1% of bacteria can be adhered on the surface due to the lower surface roughness and negative charge surface by PEDOT/PSS and PEDOT/GO modification. Furthermore, the anti-bacterial capability (7 mm of inhibition zone) was observed after adding PDDA on the PEDOT/GO substrates, suggesting that the positive charge of the PEDOT/GO/PDDA substrate can effectively kill bacteria (Staphylococcus aureus). Given their anti-fouling and anti-bacterial capabilities, PEDOT derivative nanohybrid coatings have the potential to be applied to biomedical devices such as cardiovascular stents and surgical apparatus.