Two dimensional (2D) porous carbon nanosheets (CNS) have attracted tremendous research interests in energy storage and conversion, such as supercapacitors (SCs) and lithium-sulfur batteries, because of their unique micromorphology, chemical stability and high specific surface area (SSA). Rational design and facile scalable synthesis of

No abstract

__________________________________________________________________________________________Please note that where the full text version provided on GALA is not the final published version, the version made available will be the most up-to-date full-text (post-print) version as provided by the author(s). Where possible, or if citing, it is recommended that the publisher's (definitive) version be consulted to ensure any subsequent changes to the text are noted. Citation for this version held on GALA:Chen, Jinhu, Trevarthen, James A., Deng, Tong, Bradley, Michael S.A., Rahatekar, Sameer S. and Koziol, Krzysztof K.K. (2014) This is a PDF file of an unedited manuscript that has been accepted for publication. As a service to our customers we are providing this early version of the manuscript. The manuscript will undergo copyediting, typesetting, and review of the resulting proof before it is published in its final form. Please note that during the production process errors may be discovered which could affect the content, and all legal disclaimers that apply to the journal pertain. AbstractThe erosive wear behaviour of epoxy composites reinforced with aligned, as-produced carbon nanotube (CNT) films was investigated. The CNT film composites were fabricated in two different configurations, where the unidirectional (0°) and bi-directional (0°/90°) aligned CNT films were exposed to the particle stream. Results have shown that the unidirectional (0°) CNT film/epoxy composite exhibit superior erosive wear resistance compared to the unidirectional (0°) carbon fibre reinforced epoxy composite.Furthermore, the bi-directional (0°/90°) CNT film/epoxy composite shows even better resistance to erosion compared to the unidirectional (0°) CNT film/epoxy composite due to additional impact energy absorption resulted from CNT networks. Scanning Electron Microscopy (SEM) provides further insight into the erosive wear mechanisms of CNT film composites at different impingement angles. This work has successfully introduced aligned as-produced CNT films fabricating epoxy composites using