Fluorescent nanodiamond is a new nanomaterial that possesses several useful properties, including good biocompatibility, excellent photostability and facile surface functionalizability. Moreover, when excited by a laser, defect centres within the nanodiamond emit photons that are capable of penetrating tissue, making them well suited for biological imaging applications. Here, we show that bright fluorescent nanodiamonds can be produced in large quantities by irradiating synthetic diamond nanocrystallites with helium ions. The fluorescence is sufficiently bright and stable to allow three-dimensional tracking of a single particle within the cell by means of either one- or two-photon-excited fluorescence microscopy. The excellent photophysical characteristics are maintained for particles as small as 25 nm, suggesting that fluorescent nanodiamond is an ideal probe for long-term tracking and imaging in vivo, with good temporal and spatial resolution.

Carboxylated/oxidized diamond nanoparticles (nominal size 100 nm) exhibit exceptionally high affinity for proteins through both hydrophilic and hydrophobic forces. The affinity is so high that proteins in dilute solution can be easily captured by diamonds, simply separated by centrifugation, and directly analyzed by matrix-assisted laser desorption/ionization (MALDI) time-of-flight (TOF) mass spectrometry (MS). No preseparation of the adsorbed molecules from diamonds is required for the mass spectrometric analysis. Compared to conventional MALDI-TOF-MS, an enhancement in detection sensitivity by more than 2 orders of magnitude is achieved for dilute solution containing cytochrome c, myoglobin, and albumin because of preconcentration of the probed molecules. The lowest concentration detectable is 100 pM for a 1-mL solution. Aside from the enhanced sensitivity, the overall performance of this technique does not show any sign of deterioration for highly contaminated protein solutions, and furthermore, no significant peak broadening and band shift were observed in the mass spectra. The promise of this new method for clinical proteomics research is demonstrated with an application to human blood serum.

No abstract

Two-photon fluorescence spectroscopy of negatively charged nitrogen-vacancy [(N-V)-] centers in type Ib diamond single crystals have been studied with a picosecond (7.5 ps) mode-locked Nd:YVO(4) laser operating at 1064 nm. The (N-V)- centers were produced by radiation damage of diamond using a 3 MeV proton beam, followed by thermal annealing at 800 degrees C. Prior to the irradiation treatment, infrared spectroscopy of the C-N vibrational modes at 1344 cm(-1) suggested a nitrogen content of 109 +/- 10 ppm. Irradiation and annealing of the specimen led to the emergence of a new absorption band peaking at approximately 560 nm. From a measurement of the integrated absorption intensity of the sharp zero-phonon line (637 nm) at liquid nitrogen temperature, we determined a (N-V)- density of (4.5 +/- 1.1) x 10(18) centers/cm3 (or 25 +/- 6 ppm) for the substrate irradiated at a dose of 1 x 1016) H(+)/cm(2). Such a high defect density allowed us to observe two-photon excited fluorescence and measure the corresponding fluorescence decay time. No significant difference in the spectral feature and fluorescence lifetime was observed between one-photon and two-photon excitations. Assuming that the fluorescence quantum yields are the same for both processes, a two-photon absorption cross section of sigma(TPA) = (0.45 +/- 0.23) x 10(-50) cm(4).s/photon at 1064 nm was determined for the (N-V)- center based on its one-photon absorption cross section of sigma(OPA) = (3.1 +/- 0.8) x 10(-17) cm2 at 532 nm. The material is highly photostable and shows no sign of photobleaching even under continuous two-photon excitation at a peak power density of 3 GW/cm(2) for 5 min.