AbstractZirconium thin films were grown on high carbon steel substrates EN C100 (1 %wt. of carbon) by RF magnetron sputtering. In order to study the reactivity of the film/substrate system as a function of the temperature, one hour vacuum annealing was carried out for different temperatures between 600°C and 1100°C. The films were then analyzed by X-ray diffraction, scanning electron microscopy, glow discharge optical emission spectroscopy (GDOES) and nanoindentation.The obtained results showed a progressive transformation of zirconium film to zirconium carbide.Carbon atoms diffusion from substrate toward the film induced this transformation. The sample annealed at 900°C exhibited the best mechanicals properties (H =17 GPa and E = 220 GPa).Samples treated at higher temperature were affected by oxidation and high microporosity. Even if the conversion is uncomplete, annealing significantly promotes adhesion of the film on the substrate.
This study applies the Taguchi method to investigate the relationship between the ultimate tensile strength, hardness and process variables in a squeeze casting 2017 A wrought aluminium alloy. The effects of various casting parameters including squeeze pressure, melt temperature and die temperature were studied. Therefore, the objectives of the Taguchi method for the squeeze casting process are to establish the optimal combination of process parameters and to reduce the variation in quality between only a few experiments. The experimental results show that the squeeze pressure significantly affects the microstructure and the mechanical properties of 2017 A Al alloy.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.