Although microarc oxidation is frequently used in producing wear‐ and corrosion‐resistant coatings on Ti and Ti alloys for biomedical applications, the formation of nonuniform microstructure of the coatings is still unavoidable. To overcome this drawback, this work adopts ultrasonic assistance in the microarc oxidation of Ti–6Al–4V and systematically investigates the influences of ultrasonic treatment with different durations on the coating microstructures and resultant properties. The positive effects of ultrasonic, such as cavitation effect, sound flow effect, and mechanical effect, accelerate the cooling rate of electrolyte and promote the homogeneity of the solute on the sample surface. Therefore, the ultrasonic‐assisted coatings exhibit uniform microstructures with fewer cracks and therefore improve performances. For instance, compared with the counterpart without ultrasonic assistance, the ultrasonic‐assisted coating with 15 min duration demonstrates 25.1% lower mass loss in the tribology test and half corrosion density in Hank's solution. Such results indicate that ultrasonic assistance in microarc oxidation of Ti–6Al–4V can homogenize the microstructures of coatings and enhance their corrosion resistance and wear resistance in human body.

In this paper the effect of solution treatment on the corrosion resistance of welding joint of Ni56Cr22Mo13 alloy was studied by polarization curves, mass loss method, SEM. The results indicated that the composition of alloy welded was not uniform and the corrosion resistance of welding joint of Ni56Cr22Mo13 alloy was poor. After solution treatment, the corrosion resistance was enhanced.