No abstract

Improving the strength of the bonding of zirconia to composite resins remains a challenge in dental restorations. The purpose of this study was to evaluate the shear strength of the bonding of zirconia to composite resins, thereby verifying the hypothesis that as the power of the non-thermal oxygen plasma increases, the bonding strength of the plasma-treated zirconia is increased. The effects of the oxygen plasma power (100, 200, and 400 W) on the surface structure, chemical composition, and hydrophilicity of the zirconia and the strength of the bonding between zirconia and composite resin were investigated. As a result, after different plasma power treatments, the surface structure and phase composition of zirconia were not different from those of zirconia without treatment. However, the oxygen plasma treatment not only reduced carbon adsorption but also greatly increased the hydrophilicity of the zirconia surface. More importantly, the strength of the bonding between the plasma-treated zirconia and composite resin was significantly higher than that in the corresponding control group without plasma treatment. Regardless of whether the zirconia was pristine or sandblasted, the higher the plasma power, the greater the bond strength obtained. The conclusion is that the oxygen plasma treatment of zirconia can effectively improve the strength of the bonding between the zirconia and composite resin without damaging the microstructure and phase composition of the zirconia.

Background/purpose With the technology of dental prostheses and materials progress, the bond durability of the all-ceramic restoration system plays an important role in the oral environment. The purpose of this study was to evaluate the influence of the parameters of blasting on the shear bond strength between zirconia and pressed veneer ceramics. Materials and methods Zirconia was blasted with different alumina particle size subjected to two types of applied pressures. Heat-pressed and layered veneer ceramic blocks were served as an experimental group and control group, respectively. The shear strength of specimens after thermocycling for 20,000 times was also investigated to simulate oral environment. Results The results indicated that the surface roughness was increased significantly (P < 0.05) with increasing particle size of alumina and blasting pressure. The alumina particle size had statistically significant influence (P < 0.05) on shear strength of heat-pressed groups. Among heat-pressed ceramic specimens, the highest and lowest shear strength could be obtained when 50 μm of alumina was used at pressure of 0.3 MPa and 110 μm of alumina was used at 0.5 MPa, respectively. The negligible effect of thermal cycle on shear strength of heat-pressed groups can be seen. Conclusion Blasting with 50 μm of alumina at 0.3 MPa could enhance the bond strength between zirconia and veneer ceramics.

Background/purpose The efficient rapid sintering technique has employed to dental zirconia ceramics for shortening the fabrication time of zirconia restorations. The purpose was to compare the optical properties of two generations of rapid sintered translucent zirconia using two dental colorimeters. Materials and methods Two generations of translucent zirconia ceramics, 3 mol% yttria-tetragonal zirconia polycrystal (3Y-TZP): Copran Zr-i Ultra-T (UT) and Cercon HT (HT), and 5 mol% yttria-tetragonal zirconia polycrystal (5Y-TZP): Cercon xt (XT), of different thicknesses (0.5, 0.8, and 1.2 mm; n = 5) underwent rapid sintering (RS) or conventional sintering (CS). The CIELAB values were measured on the white and black backgrounds, respectively, by digital colorimeters, shadepilot, DeguDent (DD) and Easyshade V, Vita (Vita). Translucency parameter (TP), color difference (ΔE), surface morphology, and surface roughness were evaluated. Results RS resulted in reduced lightness, except in the XT group. The chromaticity increased slightly after RS. Translucency decreased with increasing material thickness. ΔE values differed between both sintering processes but were clinically acceptable (ΔE < 5). Grain size of XT decreased after RS. RS did not affect the surface roughness. Conclusion RS is a feasible method for shortening the manufacturing time of zirconia restorations. A significant difference in TP value was only in the XT group between both sintering methods as measured on DD. Color differences in rapid sintered translucent zirconia materials are imperceptible and acceptable. The specimen thickness affected more in the TP values of Vita than DD. DD has higher sensitivity to translucency and color compared with Vita.