The adoption of magnetic hyperthermia as either a stand-alone or adjunct therapy for cancer is still far from being optimised due to the variable performance found in many iron oxide nanoparticle systems, including commercially available formulations. Herein, we present a reproducible and potentially scalable microwave-based method to make stable citric acid coated multi-core iron oxide nanoparticles, with exceptional magnetic heating parameters, viz. intrinsic loss parameters (ILPs) of up to 4.1 nH m(2) kg(-1), 35% better than the best commercial equivalents. We also probe the core-to-core magnetic interactions in the particles via remanence-derived Henkel and ΔM plots. These reveal a monotonic dependence of the ILP on the magnetic interaction field Hint, and show that the interactions are demagnetising in nature, and act to hinder the magnetic heating mechanism.

Iron oxide nanoparticles are widely used for biological applications thanks to their outstanding balance between magnetic properties, surface-to-volume ratio suitable for efficient functionalization and proven biocompatibility. Their development for MRI or magnetic particle hyperthermia concentrates much of the attention as these nanomaterials are already used within the health system as contrast agents and heating mediators. As such, the constant improvement and development for better and more reliable materials is of key importance. On this basis, this review aims to cover the rational design of iron oxide nanoparticles to be used as MRI contrast agents or heating mediators in magnetic hyperthermia, and reviews the state of the art of their use as nanomedicine tools.

Three different magnetic samples with particle sizes ranging from 10 to 30 nm were prepared by wet chemical methods. The powders were heated at 100, 150, 200, and 250 °C during 30 min under air. Ferrous and total iron contents were determined immediately after the synthesis and after the thermal treatments. All samples were characterized by X-ray diffraction, transmission and integral low-energy electron Mössbauer spectroscopy (ILEEMS) at 298 K. These samples are composed of a mixture of individual particles of maghemite and magnetite, which implies that once oxidation starts in this kind of material, it occurs throughout the entire particle volume. The existence of a maghemite/magnetite core-shell model was ruled out. A linear correlation between the average isomer shift and the magnetite content was found, allowing the estimation of the amounts of magnetite and maghemite in an unknown sample without the need of performing chemical analysis.

Our observations support the proposition that intracellular heating may be a viable, controllable and nonaggressive in vivo treatment for human pathological conditions.