Brackets are metallic dental devices that are very often associated with acidic soft drinks such as cola and energy drinks. Acid erosion may affect the bonding between brackets and the enamel surface. The purpose of this study was to investigate the characteristics of brackets’ adhesion, in the presence of two different commercially available drinks. Sixty human teeth were divided into six groups and bonded with either resin-modified glass ionomer (RMGIC) or resin composite (CR). A shared bond test (SBS) was evaluated by comparing two control groups with four other categories, in which teeth were immersed in either Coca-ColaTM or Red BullTM energy drink. The debonding between the bracket and enamel was evaluated by SEM. The morphological aspect correlated with SBS results showed the best results for the samples exposed to artificial saliva. The best adhesion resistance to the acid erosion environment was observed in the group of teeth immersed in Red BullTM and with brackets bonded with RMGIC. The debonded structures were also exposed to Coca-ColaTM and Red BullTM to assess, by atomic force microscopy investigation (AFM), the erosive effect on the enamel surface after debonding and after polishing restoration. The results showed a significant increase in surface roughness due to acid erosion. Polishing restoration of the enamel surface significantly reduced the surface roughness that resulted after debonding, and inhibited acid erosion. The roughness values obtained from polished samples after exposure to Coca-ColaTM and Red BullTM were significantly lower in that case than for the debonded structures. Statistical results evaluating roughness showed that Red BullTM has a more erosive effect than Coca-Cola™. This result is supported by the large contact surface that resulted after debonding. In conclusion, the prolonged exposure of the brackets to acidic drinks affected the bonding strength due to erosion propagation into both the enamel–adhesive interface and the bonding layer. The best resistance to acid erosion was obtained by RMGIC.

The present research is focused on three different classes of orthodontic cements: resin composites (e.g., BracePaste); resin-modified glass ionomer RMGIC (e.g., Fuji Ortho) and resin cement (e.g., Transbond). Their mechanical properties such as compressive strength, diametral tensile strength and flexural strength were correlated with the samples’ microstructures, liquid absorption, and solubility in liquid. The results show that the best compressive (100 MPa) and flexural strength (75 Mpa) was obtained by BracePaste and the best diametral tensile strength was obtained by Transbond (230 MPa). The lowestvalues were obtained by Fuji Ortho RMGIC. The elastic modulus is relatively high around 14 GPa for BracePaste, and Fuji Ortho and Transbond have only 7 GPa. The samples were also subjected to artificial saliva and tested in different acidic environments such as Coca-Cola and Red Bull. Their absorption and solubility were investigated at different times ranging from 1 day to 21 days. Fuji Ortho presents the highest liquid absorption followed by Transbond, the artificial saliva has the best absorption and Red Bull has the lowest absorption. The best resistance to the liquids was obtained by BracePaste in all environments. Coca-Cola presents values four times greater than the ones observed for artificial saliva. Solubility tests show that BracePaste is more soluble in artificial saliva, and Fuji Ortho and Transbond are more soluble in Red Bull and Coca-Cola. Scanning electron microscopy (SEM) images evidenced a compact structure for BracePaste in all environments sustaining the lower liquid absorption values. Fuji Ortho and Transbond present a fissure network allowing the liquid to carry out in-depth penetration of materials. SEM observations are in good agreement with the atomic force microscopy (AFM) results. The surface roughness decreases with the acidity increasing for BracePaste meanwhile it increases with the acidity for Fuji Ortho and Transbond. In conclusion: BracePaste is recommended for long-term orthodontic treatment for patients who regularly consume acidic beverages, Fuji Ortho is recommended for short-term orthodontic treatment for patients who regularly consume acidic beverages and Transbond is recommended for orthodontic treatment over an average time period for patients who do not regularly consume acidic beverages.