We show that natural abundance oxygen-17 NMR of solids could be obtained in minutes at a moderate magnetic field strength by using dynamic nuclear polarization (DNP). Electron spin polarization could be transferred either directly to (17)O spins or indirectly via (1)H spins in inorganic oxides and hydroxides using an oxygen-free solution containing a biradical polarization agent (bTbK). The results open up a powerful method for rapidly acquiring high signal-to-noise ratio solid-state NMR spectra of (17)O nuclear spins and to probe sites on or near the surface, without the need for isotope labeling.

This Communication describes the synthesis of highly monodispersed 12 nm nickel nanocubes. The cubic shape was achieved by using trioctylphosphine and hexadecylamine surfactants under a reducing hydrogen atmosphere to favor thermodynamic growth and the stabilization of {100} facets. Varying the metal precursor to trioctylphosphine ratio was found to alter the nanoparticle size and shape from 5 nm spherical nanoparticles to 12 nm nanocubes. High-resolution transmission electron microscopy showed that the nanocubes are protected from further oxidation by a 1 nm NiO shell. Synchrotron-based X-ray diffraction techniques showed the nickel nanocubes order into [100] aligned arrays. Magnetic studies showed the nickel nanocubes have over 4 times enhancement in magnetic saturation compared to spherical superparamagnetic nickel nanoparticles.

No abstract

Branched metal nanostructures are of great technological importance because of their unique size- and shape-dependent properties. A kinetically controlled synthesis that uses polymorphism to produce branched nickel nanoparticles is presented. These nanoparticles consist of a face-centred cubic (fcc) core and extended arms of alternating fcc and hexagonal close-packed (hcp) nickel phases.

No abstract