Bulk oxyfluoride glasses doped with Ag nanoclusters have been prepared using the melt quenching technique. When pumped in the absorption band of Ag nanoclusters between 300 to 500 nm, these glasses emit a very broad luminescence band covering all the visible range with a weak tail extending into the near infrared. The maximum of the luminescence band and its color shifts to the blue with a shortening of the excitation wavelength and an increasing ratio of oxide to fluoride components, resulting in white color luminescence at a particular ratio of oxide to fluoride; with a quantum yield above 20%.
in this paper we present a facile method for the synthesis of aminated graphene derivative through simultaneous reduction and amination of graphene oxide via two-step liquid phase treatment with hydrobromic acid and ammonia solution in mild conditions. the amination degree of the obtained aminated reduced graphene oxide is of about 4 at.%, whereas C/O ratio is up to 8.8 as determined by means of X-ray photoelectron spectroscopy. the chemical reactivity of the introduced amine groups is further verified by successful test covalent bonding of the obtained aminated graphene with 3-Chlorobenzoyl chloride. The morphological features and electronic properties, namely conductivity, valence band structure and work function are studied as well, illustrating the influence of amine groups on graphene structure and physical properties. particularly, the increase of the electrical conductivity, reduction of the work function value and tendency to form wrinkled and corrugated graphene layers are observed in the aminated graphene derivative compared to the pristine reduced graphene oxide. As obtained aminated graphene could be used for photovoltaic, biosensing and catalysis application as well as a starting material for further chemical modifications.
We report on the thorough investigation of light emitting diodes (LEDs) made of core-shell nanorods (NRs) with InGaN/GaN quantum wells (QWs) in the outer shell, which are grown on patterned substrates by metal-organic vapor phase epitaxy. The multi-bands emission of the LEDs covers nearly the whole visible region, including UV, blue, green, and orange ranges. The intensity of each emission is strongly dependent on the current density, however the LEDs demonstrate a rather low color saturation. Based on transmission electron microscopy data and comparing them with electroluminescence and photoluminescence spectra measured at different excitation powers and temperatures, we could identify the spatial origination of each of the emission bands. We show that their wavelengths and intensities are governed by different thicknesses of the QWs grown on different crystal facets of the NRs as well as corresponding polarization-induced electric fields. Also the InGaN incorporation strongly varies along the NRs, increasing at their tips and corners, which provides the red shift of emission. With increasing the current, the different QW regions are activated successively from the NR tips to the side-walls, resulting in different LED colors. Our findings can be used as a guideline to design effectively emitting multi-color NR-LEDs.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.