Microcapsules, with sodium silicate solution as core, were produced using complex coacervation in a double, oil-in-water-in oil, emulsion system. The shell material was a gelatin-acacia gum crosslinked coacervate and the produced microcapsules had diameters ranging from 300 to 700 μm. The shell material designed with switchable mechanical properties. When it is hydrated exhibits soft and 'rubbery' behaviour and, when dried, transitions to a stiff and 'glassy' material. The microcapsules survived drying and rehydrating cycles and preserved their structural integrity when exposed to highly alkaline solutions that mimic the pH environment of concrete. Microscopy revealed that the shell thickness of the microcapsules varies across their perimeter from 5 to 20 μm. Thermal analysis showed that the produced microcapsules were very stable up to 190°C. Proof of concept investigation has demonstrated that the microcapsules successfully survive and function when exposed to a cement-based matrix. Observations showed that the microcapsules survive mixing with cement and rupture successfully upon crack formation releasing the encapsulated sodium silicate solution.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.