We report that crystalline phases with ferroelectric behavior can be formed in thin films of SiO2 doped hafnium oxide. Films with a thickness of 10 nm and with less than 4 mol%. of SiO2 crystallize in a monoclinic/tetragonal phase mixture. We observed that the formation of the monoclinic phase is inhibited if crystallization occurs under mechanical encapsulation and an orthorhombic phase is obtained. This phase shows a distinct piezoelectric response, while polarization measurements exhibit a remanent polarization above 10 C/cm2 at a coercive field of 1 MV/cm, suggesting that this phase is ferroelectric. Ferroelectric hafnium oxide is ideally suited for ferroelectric field effect transistors and capacitors due to its excellent compatibility to silicon technology
The transition metal oxides ZrO(2) and HfO(2) as well as their solid solution are widely researched and, like most binary oxides, are expected to exhibit centrosymmetric crystal structure and therewith linear dielectric characteristics. For this reason, those oxides, even though successfully introduced into microelectronics, were never considered to be more than simple dielectrics possessing limited functionality. Here we report the discovery of a field-driven ferroelectric phase transition in pure, sub 10 nm ZrO(2) thin films and a composition- and temperature-dependent transition to a stable ferroelectric phase in the HfO(2)-ZrO(2) mixed oxide. These unusual findings are attributed to a size-driven tetragonal to orthorhombic phase transition that in thin films, similar to the anticipated tetragonal to monoclinic transition, is lowered to room temperature. A structural investigation revealed the orthorhombic phase to be of space group Pbc2(1), whose noncentrosymmetric nature is deemed responsible for the spontaneous polarization in this novel, nanoscale ferroelectrics.
We report the observation of ferroelectricity in capacitors based on hafnium-zirconium-oxide. Hf0.5Zr0.5O2 thin films of 7.5 to 9.5 nm thickness were found to exhibit ferroelectric polarization-voltage hysteresis loops when integrated into TiN-based metal-insulator-metal capacitors. A remnant polarization of 16 μC/cm2 and a high coercive field of 1 MV/cm were observed. Further proof for the ferroelectric nature was collected by quasi-static polarization-voltage hysteresis, small signal capacitance-voltage, and piezoelectric measurements. Data retention characteristics were evaluated by a Positive Up Negative Down pulse technique. No significant decay of the initial polarization state was observed within a measurement range of up to two days.
We investigated phase transitions in ferroelectric silicon doped hafnium oxide (FE-Si:HfO2) by temperature dependent polarization and x-ray diffraction measurements. If heated under mechanical confinement, the orthorhombic ferroelectric phase reversibly transforms into a phase with antiferroelectric behavior. Without confinement, a transformation into a monoclinic/tetragonal phase mixture is observed during cooling. These results suggest the existence of a common higher symmetry parent phase to the orthorhombic and monoclinic phases, while transformation between these phases appears to be inhibited by an energy barrier
We report the discovery of ferroelectricity in crystalline hafnium silicon oxide. If HfO2 based thin films, at a composition where the tetragonal phase is not yet stable, are crystallized in presence of a cap, the formation of an orthorhombic phase is observed. o-HfO2 shows a piezoelectric response, while a polarization measurements exhibit a remanent polarization above 10 µC/cm2 at a coercive field of 1 MV/cm, confirming this phase to be ferroelectric. Transistors fabricated with this material exhibit a permanent and switchable shift of the threshold voltage, allowing the realization of CMOS-compatible ferroelectric field effect transistors (FeFET) with sub 10 nm gate insulators for the first time
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.