The influence of the chromium layer with the thickness of 1 micrometer sputter-deposited on the X33CrNiMn23-8 and X50CrMnNiNbN21-9 steel surfaces on the oxidation behavior of these steels has been studied at 1173 K in air, using the microthermogravimetric technique. It has been found that coated materials show very good oxidation resistance under isothermal conditions, comparable with that of chromia formers, due to the formation of Cr 2 O 3 scales on their surfaces. It has been also demonstrated that the positive effect of chromium addition on the oxidation resistance of investigated steels is observed during a much longer period of time than the life-time of the chromium coating.Keywords: valve steels, coatings, oxidation W pracy zbadano metodą grawimetryczną wpływ warstwy chromu o grubości 1 mikrometra, nałożonej metodą magnetronową na powierzchnie stali X33CrNiMn23-8 i X50CrMnNiNbN21-9, na kinetykę utleniania tych stali w temperaturze 1173 K w powietrzu. Przeprowadzone badania wykazały, że stale pokryte powłoką wykazują bardzo dobrą odporność na utlenianie w warunkach izotermicznych, porównywalną do tej, jaką charakteryzują się stopy z grupy chromia formers, w wyniku powstawania na ich powierzchni zgorzeliny zbudowanej z Cr 2 O 3 . Wykazano również, że korzystny wpływ dodatku chromu na odporność na utlenianie badanych stali obserwowany jest przez znacznie dłuższy czas od czasu stabilności samej powłoki.