Currently, the use of composites to replace parts made only with plastics has been gradually employed. The advantages of these composites are low cost, high availability of raw materials and good physical and mechanical properties. Thus, this work aimed at producing and characterizing composites produced with coconut fibre reinforced polyurethane matrices. The coconut fibres were studied as to their chemical constituents, aspect ratio, bulk density, pH, tensile properties, and surface SEM images. The composites were prepared using the hand lay-up process and four different concentrations of coconut fibre were evaluated: 30, 40, 50, and 60%. The composites were assessed as for water absorption after 20 days of immersion, bulk density, impact IZOD, tensile tests, and visualize the matrix-reinforcement interface using SEM. The electron micrographs showed a great deal of impurities on the surface of coconut fibres, such as greases, waxes, and gums, due to the high amount of extraction material (19.78%), which damages the adherence of the polymer onto the coconut fibre and, as observed, cause detachment between the reinforcement and the matrix. The tensile strength of the composites tended to increase as greater amounts of coconut fibres were added to the matrix. The averages were around 6.51 to 6.72 MPa for composites with 30 and 60% fibres, respectively. Therefore, coconut fibres can be considered as an alternative to synthetic fibres commonly used in composites, and they can be used at a ratio of 60% without prejudicing the properties of the composites, making them lighter and cheaper.

The use of the Hevea brasiliensis tree in latex rubber production has resulted in a consolidated role of this tree in the Brazilian economy. However, at the end of the productive cycle of the tree that lasts for approximately 25 years, the timber resulting from this venture has no added value and is usually used for the production of firewood. In order to introduce this species into the furniture and civil construction industry, the current study aimed to evaluate the quality of particleboard produced by adding Pinus oocarpa wood with Hevea brasiliensis wood in different ratios. The particleboards were produced with a nominal density of 0.60 g/cm³ and 8% (wt%) urea-formaldehyde resin and pressed at 160 °C for 8 min at a pressure of 4.0 MPa. The quality of the particleboard was evaluated by water absorption and thickness swelling, internal bonding, static bending, and screw withdrawal tests. The substitution of Pinus particles by Hevea wood resulted in decreased water absorption and thickness swelling. The boards produced with a higher proportion of Hevea had better dimensional stability due to the greater porosity of the Pinus oocarpa particles. The inclusion of Hevea brasiliensis wood resulted in a 75% increase in the modulus of rupture and a 300% increase in internal bonding compared with the particleboards produced only with Pinus oocarpa wood. The results show that Hevea brasiliensis wood could be used to obtain higher value-added products and contribute to the diversification of the raw materials used in the particleboard industries of Brazil.

O objetivo deste trabalho foi avaliar as propriedades físicas e mecânicas de chapas de madeira aglomerada utilizando partículas oriundas de maravalhas a três teores de adesivo fenol-formaldeído, 6, 9 e 12% (base massa seca). Os painéis foram produzidos com densidade nominal de 0,70 g.cm-3, ciclo de prensagem com temperatura de 160 °C, pressão de 3,92 MPa e tempo de 8 minutos. Foram avaliadas as propriedades de absorção de água (AA), inchamento em espessura (IE), ambas após 2 e 24 horas, densidade aparente, razão de compactação, tração perpendicular, módulo de elasticidade (MOE) e módulo de ruptura (MOR) na flexão estática e resistência ao arranchamento de parafuso. Os resultados dos testes indicaram que com o aumento do teor de adesivo de 6 para 12%, não houve diferença estatística significativa para os valores médios de densidade aparente e razão de compactação, sendo eles 0,624 g.cm-3 e 1,234, respectivamente, e diminui-se a AA e o IE após 2 e 24 horas. Houve um ganho de 49% para MOR e 40% para MOE. Para tração perpendicular, os maiores valores médios foram referentes ao painel com 12% de adesivo. Já para arrancamento de parafuso, os painéis não atenderam às normas vigentes.

A construção civil apresenta dados alarmantes no que diz respeito à exposição dos trabalhadores aos riscos ocupacionais os quais existem nas mais diversas atividades que o setor oferece, colocando em risco a saúde e integridade física desses colaboradores. Nesse sentido, o presente trabalho teve por objetivo aplicar a técnica de análise preliminar de riscos nas atividades executadas pelos trabalhadores e no processo construtivo de uma obra residencial unifamiliar no município de Candeias, Minas Gerais. Para isso, foram verificadas as condições dos equipamentos utilizados, análise do ambiente laboral, verificação dos dispositivos de proteção individual e coletivos, bem como as instalações das máquinas e equipamentos. A partir dos dados obtidos foram realizadas a análise dos riscos existentes e estudo da severidade e probabilidade dos mesmos. A análise foi feita observando os métodos de trabalho realizados rotineiramente na obra. Após o reconhecimento dos riscos, estes foram apresentados e discutidos com os colaboradores para que fosse possível propor medidas de controle afim de reduzir ou eliminar tais riscos, bem como, proporcionar treinamentos e uma maior conscientização nesse ambiente laboral.