No abstract

Cardiovascular disease is the most common cause of death in the world. In severe cases, replacement or revascularization using vascular grafts are the treatment options. While several synthetic vascular grafts are clinically used with common approval for medium to large-caliber vessels, autologous vascular grafts are the only options clinically approved for small-caliber revascularizations. Autologous grafts have, however, some limitations in quantity and quality, and cause an invasiveness to patients when harvested. Therefore, the development of small-caliber synthetic vascular grafts (<5 mm) has been urged. Since small-caliber synthetic grafts made from the same materials as middle and large-caliber grafts have poor patency rates due to thrombus formation and intimal hyperplasia within the graft, newly innovative methodologies with vascular tissue engineering such as electrospinning, decellularization, lyophilization, and 3D printing, and novel polymers have been developed. This review article represents topics on the methodologies used in the development of scaffold-based vascular grafts and the polymers used in vitro and in vivo.

Bio-electrospraying (BES) is a technique used for the processing of cells and can be applied to tissue engineering. The association of BES with scaffold production techniques has been shown to be an interesting strategy for the production of biomaterials with cells homogeneously distributed in the entire structure. Various studies have evaluated the effects of BES on different cell types. However, until the present moment, no studies have evaluated the impact of BES time on mesenchymal stem cells (MSC). Therefore, the aim of this work was to standardise the different parameters of BES (voltage, flow rate, and distance of the needle from the collecting plate) in relation to cell viability and then to evaluate the impact of BES time in relation to viability, proliferation, DNA damage, maintenance of plasticity and the immunophenotypic profile of MSC. Using 15 kV voltage, 0.46 ml/h flow rate and 4 cm distance, it was possible to form a stable and continuous jet of BES without causing a significant reduction in cell viability. Time periods between 15 and 60 min of BES did not cause alterations of viability, proliferation, plasticity, and immunophenotypic profile of the MSC. Time periods above 30 min of BES resulted in DNA damage; however, the DNA was able to repair itself within five hours. These results indicate that bio-electrospraying is an adequate technique for processing MSC which can be safely applied to tissue engineering and regenerative medicine.

The sterilization of scaffolds is an essential step for tissue engineering in vitro and, mainly, clinical biomaterial use. However, this process can cause changes in the structure and surface of the scaffolds. Therefore, the objective of this study was to investigate the effect of sterilization by ethanol, ultraviolet radiation (UVR) or antimicrobial solution (AMS) on poly(lactide-co-glycolide) (PLGA) scaffolds produced by the electrospinning technique. The properties of nanofibers and the cellular adhesion of mesenchymal stem cells to the scaffolds were analyzed after the treatments. All methods generated sterile scaffolds but showed some kind of damage to the scaffolds. Ethanol and AMS caused changes in the morphology and scaffold dimensions, which were not observed when using the UVR method. However, UVR caused a greater reduction in polymeric molecular weight, which increased proportionally with exposure time of treatment. Nanofibers sterilized with AMS for 1 h and 2 h showed greater cellular adhesion than the other methods, demonstrating their potential as a method for sterilizing PLGA nanofibers.