An epitaxial Y2O3/YSZ/CeO2
buffer architecture has been prepared using pulsed laser deposition on cube texture
Ni–3 at.%
W/Ni–10 at.%
Cr–1.5 at.%
Al and Ni–5 at.% W/Ni–10 at.% W composite tapes. The buffer layer growth was studied in detail and
revealed good texture transfer throughout the structure, similar to standard
Ni–5 at.% W
substrates. YBCO layers were successfully deposited on the buffered tapes and compared to films grown
on SrTiO3
single crystals. A superconducting transition temperature of about 90 K with a small
transition width was observed on all metal substrates. A critical current density
Jc of
about 1 MA cm−2
was measured at 77 K in a self-field. It was found that
Jc is
mainly limited by the grain boundary network in magnetic fields below 4 T, whereas similar values as
on SrTiO3
single crystals were measured at higher fields.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.