Synthesis of 2-sulfonylquinolines via a three-component reaction of quinoline N-oxides, sodium metabisulfite, and aryldiazonium tetrafluoroborates under transition-metal- and oxidant-free conditions.

No abstract

Herein, electrospun zinc oxide nanoparticle/poly (vinylidene fluoride) (ZnONP/PVDF) composite fiber membranes were designed, fabricated, and tested for improved orthopedic applications. A single factor screening study was conducted to determine the optimal ZnONP/PVDF formulation based on osteoblast (bone forming cells) proliferation and antibacterial properties. Further, ZnONP/PVDF materials were characterized for their morphology, crystallinity, roughness, piezoelectric properties, and chemistry to understand such cell results. The optimal concentration of high molecular weight PVDF (18%, w/v) and a low concentration of ZnONPs (1 mg/ml) were identified for electrospinning at room temperature in order to inhibit bacterial colonization (without resorting to antibiotic use) and promote osteoblast proliferation. Compared to no ZnO/PVDF scaffold without Piezo-excited group,the study showed that on the 1 mg/ml ZnO/PVDF scaffolds with piezo-excitation, the density of SA and E.coli decreased by 68% and 56%.The density of osteoblasts doubled within three days(compared to the control). In summary, ZnONP/PVDF composite fiber membranes were formulated by electrospinning showing an exceptional ability to eliminate bacteria colonization while at the same time promote osteoblast functions and, thus, they should be further studied for a wide range of orthopedic applications.

Polyvinylidene fluoride (PVDF)/polymethylmethacrylate (PMMA)/thermoplastic polyurethane (TPU) blend hollow fiber membranes were successfully prepared by the wet-spinning method with the loading of PMMA and TPU in a range of polymer concentrations varying from 0 to 20 wt% and at a total polymer concentration of 16 wt%. The influence of the addition of PMMA and TPU on the morphologies and the properties of such prepared membranes was investigated through FTIR-ATR, SEM, viscosity measurements, UF experiments and mechanical strength tests. Based on the experimental results, the compatibility of the PVDF, PMMA and TPU blend was best under the conditions of the PVDF-rich phase. The elongation at break of the membrane increased to a maximum of 146% with increase in the TPU concentration to 20 wt% in dope solution. The addition of PMMA increased the water permeation flux from 120 to 195 L/(m(2) h) initially. The flux then decreased when PMMA concentration was increased to over 10 wt%. The membranes obtained at optimized blending ratio were applied to the dyeing process wastewater filtration. During continuous filtration for 8 h, the flux was stabilized at about 20 L/(m(2) h) at 0.1 MPa. The reduction in COD(Cr), turbidity and color were about 63, 84 and 63% respectively.

Poly(vinylidene fluoride)(PVDF), poly(vinyl chloride)(PVC), and poly(methyl methacrylate)(PMMA) were used as the main materials in the preparation of novel blend five-hole membrane. Dimethylacetamide (DMAC) and polyvinyl pyrrolidone (PVP) were used as solvent and additive, respectively. The effect of some external coagulation conditions on the property of five-hole membrane was studied. The external coagulation conditions investigated in the work were the coagulation temperature and the DMAC content in coagulation bath. The result showed that the flux increased along with the increase of coagulation bath temperature and could reach the max at 35°C, then decreased gradually. The effect of the DMAC content in coagulation bath on flux is very similar to that of the temperature. The cross-sectional structures were examined by scanning electron microscopy.