Copper electrodeposition on (111)-oriented Si substrate was performed by the pulsating current (PC) regime at various average current densities in the range of 15-70 mA·cm −2 , obtained by varying either the frequency (30, 50, 80 and 100 Hz for the current density amplitude of 100 mA·cm −2 ) or the current density amplitude (120 and 140 mA·cm −2 at 100 Hz). The produced Cu coatings were examined by SEM, AFM and XRD techniques. The morphology of the coatings changed from those with large grains to fine-grained and globular, while the crystal structure changed from the strong (220) to the strong (111) preferred orientation by increasing the average current density. The mechanical characteristics of coatings were examined using Vickers micro-indentation tests, applying the Chicot-Lesage (C-L) composite hardness model for the analysis of microhardness. The maximum microhardness was obtained for the Cu coating produced at an average current density of 50 mA·cm −2 , with a current density amplitude of 100 mA·cm −2 and a frequency of 100 Hz. This copper coating was fine-grained and showed the smallest roughness in relation to the other coatings, and it was obtained in the mixed activation-diffusion control between the end of the effect of the activation control and the beginning of the dominant effect of diffusion control.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.